生物可降解镁及镁基材料在口腔疾病领域的应用
赵 聪1，付慧渊1，苏尼特1，及 捷1，张 蕾1，王雅仙2
- 1 呼和浩特市口腔医院(内蒙古自治区口腔医院)，内蒙古自治区呼和浩特市 010000；2中国兵器科学研究院宁波分院，浙江省宁波市 315000
-
收稿日期:2024-07-18接受日期:2024-09-14出版日期:2025-12-08发布日期:2025-01-17 -
通讯作者:王雅仙，硕士，助理研究员，中国兵器科学研究院宁波分院，浙江省宁波市 315000 -
作者简介:赵聪，女，1993年生，内蒙古自治区巴彦淖尔市人，汉族，硕士，口腔科医师，主要从事口腔医学研究。 -
基金资助:北方材料科学与工程研究院科技创新基金项目(NBFJ2019-cly2)，项目负责人：王雅仙
Application of biodegradable magnesium and magnesium-based materials in oral diseases
Zhao Cong1, Fu Huiyuan1, Su Nite1, Ji Jie1, Zhang Lei1, Wang Yaxian2
- 1Hohhot Stomatological Hospital (Inner Mongolia Autonomous Region Stomatological Hospital), Hohhot 010000, Inner Mongolia Autonomous Region, China; 2Ningbo Branch of Chinese Academy of Weapons Science, Ningbo 315000, Zhejiang Province, China
-
Received:2024-07-18Accepted:2024-09-14Online:2025-12-08Published:2025-01-17 -
Contact:Wang Yaxian, MS, Assistant researcher, Ningbo Branch of Chinese Academy of Weapons Science, Ningbo 315000, Zhejiang Province, China -
About author:Zhao Cong, MS, Physician, Hohhot Stomatological Hospital (Inner Mongolia Autonomous Region Stomatological Hospital), Hohhot 010000, Inner Mongolia Autonomous Region, China -
Supported by:Northern Institute of Materials Science and Engineering Science and Technology Innovation Fund Project, No. NBFJ2019-cly2 (to WYX)
摘要：
文题释义：
镁：是地壳中第八丰富的元素，约占总质量的2%，是在自然界中分布最广的十大元素之一，被称为“碱土金属”。镁及镁基材料在口腔疾病领域不仅具有可降解性，还具有成骨、成血管、免疫调节等多种作用。活性氧：为细胞正常代谢的副产物，氧的部分还原代谢产物，具有强氧化能力。低浓度活性氧发挥复杂的信号传导功能，但当细胞产生的活性氧超过其抗氧化能力时可能会对细胞大分子(如脂质、蛋白质和 DNA)造成损害，导致氧化应激状态。
背景：镁及镁基材料具有良好的生物相容性、稳定的促成骨与成血管特性及免疫调节等生物活性，在口腔医学中展现出广泛的应用前景。
目的：概述生物可降解镁基材料在治疗口腔疾病中成骨、成血管及免疫调节的作用和机制，综述近年来镁及镁基材料在口腔疾病领域的应用进展。方法：以“镁，镁合金，镁基金属，骨折，种植，修复，牙髓，牙周炎，牙周疾病，囊肿，口腔癌”为中文检索关键词，以“magnesium，magnesium-based alloy，fracture，facial bone fractures，denture，dental implant，restorative dentistry，pulpitis，periodontitis，periodontal diseases，oral cancer”为英文检索关键词，在中国知网、万方、PubMed和Web of Science数据库进行检索，通过分析与筛选文献，最终纳入84篇进行归纳总结。
结果与结论：镁及镁基材料可作为颌骨骨折或正颌手术治疗的骨内固定装置，由于镁特殊的生物性能，既能保证稳定成骨又可避免二次手术的可能，具有可大范围推广使用的潜力。在口腔医学骨再生领域，镁依托其优越的生物性能表现出比现有临床材料更好的机械性能和抗菌性能，为该领域的材料发展与应用提供更多选择。借助镁的生物学活性，镁基涂层材料充分发挥抗炎抗氧化作用，进一步促进种植体骨结合及软组织整合，在种植体表面改性及促进种植体稳定方面具有较大的应用前景。镁虽在颌面部口内软组织再生与治疗、牙组织工程方面有一定的涉及，但仍存在大量空白。为保证镁稳定的生物学特性，通常需加入其他合金或进行镁表面改性，但目前对可降解金属植入物的生物学评价体系尚不完善，未来仍需进一步明确镁在口腔疾病临床中的应用。
https://orcid.org/0009-0007-8309-7141 (赵聪)
中国组织工程研究杂志出版内容重点：生物材料；骨生物材料；口腔生物材料；纳米材料；缓释材料；材料相容性；组织工程
中图分类号:
引用本文
赵 聪, 付慧渊, 苏尼特, 及 捷, 张 蕾, 王雅仙. 生物可降解镁及镁基材料在口腔疾病领域的应用[J]. 中国组织工程研究, 2025, 29(34): 7423-7430.
Zhao Cong, Fu Huiyuan, Su Nite, Ji Jie, Zhang Lei, Wang Yaxian. Application of biodegradable magnesium and magnesium-based materials in oral diseases[J]. Chinese Journal of Tissue Engineering Research, 2025, 29(34): 7423-7430.
使用本文
2.1 镁及镁基材料在口腔医学领域的发展历程 见表1。
2.2 镁及镁基材料的种类及生物学特性
2.2.1 镁及镁基材料的种类 2010年，镁及镁基材料在口腔医学上的应用研究开始大规模兴起，虽然临床研究较少，但仍有一定数量的体内外研究逐步开展。由于纯镁在机体内存在不稳定的生物学缺陷，学者们在纯镁中加入其他金属(如锌、锰、钇、铜等)制作镁基合金材料，以增强该类镁基合金材料的耐腐蚀性及生物相容性。常用于口腔医学领域体内研究的镁基金属如表2所示。
2.2.2 生物可降解性 镁及镁基材料植入后会在人体体液环境中发生降解，产生氢氧化镁、氢气和其他降解产物(图3)，其中氢氧化物会作为保护涂层附着于植入物表面，以防植入物进一步腐蚀降解[17]。人体内的巨噬细胞会吞噬部分降解产物，其余降解产物存留于骨基质中，储存在骨基质中的镁离子进一步与羟基磷灰石晶体结合，提高了羟基磷灰石晶体的溶解度，进而增加了骨强度[18]。在镁合金缓慢降解后，暂时积聚的镁离子可通过局部骨再生及循环系统释放，而不会引起血清镁离子水平的波动。正是由于这种生物可降解特性，当镁作为骨折固定物时避免了二次手术取出的风险。虽然纯镁在体内的降解产物无毒，降解产物镁离子等也能促进骨再生，但镁基植入物在体内降解过快容易导致骨折治疗失败，因此，提高镁合金植入物的耐腐蚀性是延长镁合金植入物体内固定时间的关键[19]。有研究表明，镁的降解伴随着镁离子和氢气的持续释放，增加材料表面微环境中pH值和渗透压，这些近表面效应也可能会影响残留的肿瘤细胞，具有潜在的抗肿瘤活性，如骨肉瘤的治疗[20]。
2.2.3 生物相容性 镁具有良好的生物相容性，植入后能与周围组织紧密接触且无不良反应，金属镁的密度为1.74-1.84 g/cm3，弹性模量为41-45 GPa，接近人体骨组织的密度和弹性模量(弹性模量为15-25 GPa)[21]，这些性能为镁及镁合金作为骨植入材料提供了良好的应用基础。另外，镁及镁合金降解产生的镁离子也不会对机体造成负担，因为细胞可以耐受比生理浓度大16倍的镁离子浓度。动物实验结果表明，经等离子体电解氧化锂的镁锌钙合金植入兔颅骨缺损部位后以2.32 mm/年的速率降解，没有引起兔的心、肝、肾、脾功能障碍[22]。在植入WE43镁螺钉植入治疗骨折的临床试验也未发现高镁血症的迹象，并且血中镁浓度水平正常[23]。在正颌手术患者中应用WE43镁压缩螺钉后未观察到过敏反应、肝肾功能障碍或镁血清水平升高等并发症[24]。
2.2.4 成骨特性 与传统骨内植入物(如钛、钛合金、钴铬合金)相比，镁是软组织和骨组织中的重要元素，参与许多生化反应。有研究建议健康成人每日摄入310-420 mg镁离子以维持正常的生命活动，储存24-30 g镁离子以维持基础代谢[25]。人体内的大部分镁离子储存在骨组织中，如果骨组织中的镁离子含量降低，骨组织的力学性能就会减弱，导致骨小梁断裂，增加骨折风险。即使过量的镁离子被摄入体内也可以迅速地通过循环和泌尿系统排出体外，不会造成任何损害[26]。DíAZ-TOCADOS等[27]研究证明，增加镁离子浓度可增强体外间充质干细胞的成骨作用，镁离子还通过激活Notch信号通路增强成碱性磷酸酶、Runx2、骨钙素mRNA的表达。HUNG等[28]研究发现，含10 mmol/L镁离子的细胞培养基可有效促进骨髓间充质干细胞的成骨分化，通过激活Wnt信号通路增加细胞外基质中的矿化和碱性磷酸酶表达。WANG等[29]研究证明，镁离子通过有丝分裂原活化蛋白激酶信号通路促进骨髓间充质干细胞中成骨分化标志物的表达，如骨形态发生蛋白2、Ⅰ型胶原蛋白、Runx2。有研究发现，镁提取物促进了小鼠胚胎成骨细胞前体细胞MC3T3-E1的增殖和血小板衍生生长因子分泌，从而促进了成骨细胞发育和骨形成[30]。此外，镁还促进脂肪源性基质细胞骨桥蛋白基因的表达，骨桥蛋白是早期生物材料细胞成骨相互作用的必需基因。镁离子能促进各种成骨细胞的成骨分化，这是镁应用于骨内金属植入物的基本理论依据。破骨细胞生成和成骨之间的双向平衡在骨再生中起着核心作用[31]。除了调节成骨细胞促进骨再生外，镁还可以抑制破骨细胞的生成和骨吸收[32]。
2.2.5 成血管性 对于颌面部组织重建而言，构建功能化的血管网络极其重要[33]。血管网络参与骨再生一般有膜内和软骨内骨化2种方式。在膜内骨化过程中，血管网络延伸到骨膜的间充质区域诱导分化出成骨细胞[34]；在软骨内骨化过程中，软骨模板中的非增殖软骨细胞分泌促血管生成因子以刺激血管生长，随着血管系统的扩张，软骨组织逐渐被骨组织取代，导致新骨的形成[35]。因此，促进体内血管化对骨再生至关重要。镁可调节多种内皮细胞的生物学功能，有研究表明，人脐静脉内皮细胞在一定量的镁离子中表现出高增殖率、良好的细胞形态和活力[36]。此外，一定浓度的镁离子也可以增加血管生成标志物的表达水平。YU等[10]采用等离子体浸没离子注入技术制备了一种潜在的牙种植体材料——双锌/镁离子共植入钛，以改善种植体的骨结合和长期生存，体外结果表明该系统中的镁离子通过上调人脐静脉内皮细胞中人镁离子转运蛋白的表达增加镁离子内流，通过激活缺氧诱导因子1α刺激血管内皮生长因子和血管内皮生长因子受体2的转录，从而诱导血管生成[37]。
2.2.6 免疫调节性 在骨组织工程中生物材料的骨免疫调节特性尤其受到重视，它影响着骨再生结果。免疫系统和骨骼系统共享着各种细胞因子受体和转录因子。巨噬细胞作为免疫系统的重要组成部分，包括M1型和M2型，M1型参与急性炎症，与组织修复的早期阶段密切相关；M2型在骨愈合后期发挥作用，导致主动修复或纤维组织的形成[38]。M1型和M2型巨噬细胞可以响应于各种生物材料而相互转换。巨噬细胞亚型转换过程可释放出各种成骨相关分子参与新骨形成。镁及镁基材料作为骨内金属植入物对成骨和破骨细胞有很大影响。当镁和镁合金植入体内后植入物周围的免疫反应会被触发，来自植入物的镁离子通过增强巨噬细胞向M2型极化来调节骨免疫微环境，M2型巨噬细胞分泌白细胞介素10以启动骨修复过程。此外，镁离子还可抑制M1巨噬细胞，降低促炎因子(肿瘤坏死因子α、白细胞介素6)的表达，从而起到抗炎作用。研究表明，镁合金植入后5 d和10 d显著刺激种植体-骨界面的巨噬细胞出现极化[39]。
综上所述，可降解镁基材料具有广泛的生物学活性，为其在口腔医学领域的临床应用奠定了基础。然而在免疫调节方面，目前研究仅集中于巨噬细胞所参与的组织反应，而对单核细胞、肥大细胞、T细胞和B细胞等的研究相对缺乏，以期日后进一步深入研究，完善相关免疫机制。同时，有部分学者提到的镁基材料抗肿瘤机制亦不清晰，相关详尽研究均待日后深入挖掘开展。
2.3 镁及镁基材料在口腔医学中的应用
2.3.1 镁及镁基材料在颌面部骨折中的应用 颌面部骨折大多由交通事故和暴力因素导致，对患者的外观容貌、言语和咀嚼功能都有显著影响。目前切开复位内固定是治疗颌面部骨折最常用的方法，使用的骨内固定材料多为不可降解金属，如广泛应用于临床的钛合金，尽管它具有良好的生物相容性、高耐磨性和高机械强度，但仍有一定的局限性，如可能发生暴露、感染、植入物松动及异物感等并发症，发生概率高达3%-25%[40]，并且通常还需要二次手术取出，额外的手术也无疑增加了患者的痛苦和经济负担。之后有学者发现可降解合成聚合物如聚乳酸和聚乙醇酸可作为骨内固定物使用，并解决上述问题。然而多项研究证实，合成聚合物降解可产生有毒的残留单体、磨损碎片和积累酸性中间产物，这些产物可能导致病理性骨吸收，并且这类合成聚合物的强度比钛合金弱得多，因此临床使用受到限制。纯镁在人体组织内可发生快速降解并产生氢气，不仅无法有效固定骨折断端，还可能引起周围组织气肿，但通过加入其他金属元素及表面改性技术可提高镁基合金的耐腐蚀性和生物相容性，有效解决这一问题[41-43]。
NAUJOKAT等[44]在小型猪实验中发现，WE43涂层镁合金固定面中部骨折取得了可喜效果，30周内未发生明显的降解。SCHALLER等[45]在猪眶上缘和颧骨面中截骨手术中使用WE43镁合金或聚乳酸-羟基乙酸植入物固定后，与合成聚合物聚乳酸-羟基乙酸植入物相比，镁合金具有更小的植入物尺寸和更高的机械性能，可在负载环境中支持骨折愈合。LEONHARDT等[46]与KOZAKIEWICZ等[47]对可降解镁基加压螺钉植入治疗下颌髁突骨折的临床随访观察显示，镁合金植入物固定1年后的下颌骨髁突骨质愈合良好，颞下颌关节活动度好，张口受限明显改善，虽螺钉周围显示有气体产生但无需取出。由于固定颌面部骨折时大多采用口内入路，这就要求用于颌面区域的可生物降解材料必须克服该区域特有的因素，包括附着于颌面部不同骨骼的咀嚼肌力量、唾液的特有生理环境和口腔内病原微生物的存在。镁基材料具有良好的机械强度和生物相容性，临床应用已得到证实。然而，镁基合金的抗压强度低于钛合金，这就限制了其在颌骨骨折特别是承重骨折中的应用[48]。下颌骨骨折是颌面部最常见的骨折类型，因有强大的升颌肌群和降颌肌群附着，常导致骨折块移位，咬合错乱，因此，下颌骨骨折的固定物要求有一定的机械性能。镁及镁基材料在颌面部骨折中的应用[49-53]，见表3。ORASSI等[51]通过有限元分析发现，镁合金钢板及螺钉在治疗4种下颌骨骨折类型中的固定性能表现与钛合金基本相同。ANSOMS等[52]研究显示，镁合金固定材料具有足够的机械性能承担下颌角骨折部分所承担的咀嚼力。随后有学者利用有限元分析模型模拟在正颌外科手术中使用WE43镁合金螺钉固定下颌升支矢状劈开截骨的骨折线，结果显示在咀嚼负载情况下WE43镁合金仍能稳定固定骨折线，打开了生物可降解镁合金在正颌外科方面应用的大门，提供了更多的可能性和研究方向[53-54]。
镁及镁基材料的临床应用，见表4。
2.3.2 镁及镁基材料在口腔骨再生领域中的应用
引导性骨再生技术：引导性骨再生技术中使用的引导性骨再生生物膜作为硬组织和软组织之间的屏障，可以防止软组织干扰成骨，从而为成骨细胞的分化提供足够空间，进而诱导成骨，治疗因牙周炎、拔牙、肿瘤或囊肿等疾病导致的骨缺损。临床使用的生物膜一类是可吸收的，例如合成聚合物聚乳酸-羟基乙酸、聚乙烯亚胺、聚(L-乳酸)或天然聚合物(胶原蛋白，壳聚糖)等；另一类是不可吸收的，例如钛网或聚四氟乙烯等[56]。目前临床广泛使用的胶原蛋白类可吸收生物膜虽具有良好的生物相容性与可降解性，但机械性能不足，在修复大面积及垂直性骨缺损时可能会塌陷，导致缺损部位成骨作用不足，而不可吸收类的钛网虽具有足够的机械性能，但可能需二次手术取出，应用也受到限制。多项体内外研究表明，采用热轧纯镁(镁95.5%)生物膜具有与胶原蛋白膜相当的成骨能力，并且具有良好的机械强度与缓慢降解特性，可以维持骨形成的空间，达到治疗骨高度不足及大面积骨缺损的目的[12-13]。FROSECCHI[57]将纯镁生物膜与胶原蛋白膜联合应用于治疗临床中牙槽骨的复杂骨缺损，取得了良好的成骨效果。也有学者采用不同表面处理方法提升了镁膜的免疫性及成骨性[57-61]，在降低镁膜降解率的同时也降低了骨组织细菌感染和骨吸收风险(表5)。
骨替代材料：通常同种骨、异种骨、异体骨及合成骨替代材料被用作移植材料用于颅颌面骨缺损的治疗，随着材料在医学领域的飞速发展，更多的合成材料被引入作为骨移植材料，包括钙磷陶瓷、生物玻璃及以聚乳酸为基础的可吸收聚合物。其中，钙磷陶瓷由于与骨组织的矿物组成和性质最接近而最受青睐[64]，主要以颗粒状羟基磷灰石、β-磷酸三钙盐或两者的混合物应用于临床治疗，如上颌窦底提升及拔牙后的位点保存技术[65]。但有研究证实颗粒状的磷酸钙材料也存在风险，比如可能由于其尖锐的颗粒状边缘引起上颌窦底黏膜穿孔，或者作为骨替代材料吸收率不佳，不能完全被骨组织所替代。与传统磷酸钙材料相比，镁基材料可以在中性pH值下发生化学反应产生鸟粪石(MgNH4PO4×?6H2O)等矿物，此类矿物在pH值7.01-9.62范围内具有比磷酸钙更好的吸收率，并且释放的镁离子可刺激骨骼重塑，展示出更好的溶解性和生物相容性[66]。同时，以磷酸镁为基础的镁基骨替代物大多是通过矿物粉末与水溶液混合胶凝反应加工得来，有学者通过在表面活性剂稳定的亲油性液体中乳化不同剂量比的钙镁磷水泥浆体，成功合成了具有理想尺寸分布的完全球形无创颗粒，进一步加速了镁基材料成为一种更理想骨替代材料的可能[67]。
2.3.3 镁及镁基材料在牙种植体表面涂层的应用 钛合金是牙种植体修复中应用最广泛的一种金属种植体，它可以为后期的全冠修复提供稳定基础。然而，由于纯钛种植体表面缺乏抗菌活性，种植体植入后为口腔内各种革兰阳性和阴性细菌的生长和入侵创造了良好环境，增加了感染风险，导致种植体松动[68]。因此，对钛种植体表面进行改性提高其抗菌活性、促进骨细胞附着，已成为目前解决上述问题的重要途径[69]。镁离子作为体内的重要元素参与骨愈合，通过调节体内L型钙通道降低细胞内钙浓度，可抑制种植体植入后活性氧的产生，以此减少炎症因子释放，进而发挥抗炎和抗氧化作用[70]；此外，镁离子可以随尿排泄，通过肾小管重吸收，具有良好的体内生物降解性。有体外研究结果表明，镁基涂层钛植入物可增强骨髓间充质干细胞的增殖、增加成骨标志物(碱性磷酸酶、骨钙素、骨桥蛋白、骨唾液蛋白、Runx2)的表达、增加Ⅰ型胶原沉积和抗菌活性，同时，镁离子通过调节血清钙、磷水平预防局部高钙、高磷，从而避免局部矿化，更好地促进骨愈合[71-73]。有学者将通过半粉末冶金技术将石墨烯纳米片和碳纳米管纳米系统作为增强体均匀分散在镁锌合金涂层的钛种植体中，可显著降低种植体外周的炎症反应和氧化应激，更好地抑制口腔中革兰阳性菌的生长，促进人牙龈成纤维细胞的增殖活性和成骨细胞的分化潜能，从而提高种植体的骨整合稳定性[74]。
2.3.4 镁及镁基材料在颌面部、口腔内软组织再生及牙组织工程中的应用 多项研究表明，镁及镁基材料在颌面部及口腔内软组织再生领域亦有良好的应用前景。镁对人成纤维细胞的迁移、黏附和口腔黏膜再生有积极作用。镁对成纤维细胞活性的影响可能对种植体表面改性和促进种植体颈部周围软组织愈合有良好影响。有研究表明，镁基金属植入物在降解过程中会释放出可溶的镁离子和氢气，具有神经保护和抗氧化作用[75]，中间产物镁石榴石B可通过磷脂酰肌醇3-激酶-蛋白激酶B信号转导促进神经干细胞分化、刺激局部神经再生、改善微循环，这与镁离子促进成骨的信号通路相吻。镁对神经疼痛的治疗有一定效果，补充镁对颌面部周围神经损伤的恢复也有效果，但镁在运动神经中的应用有待进一步研究。在牙组织工程方面，镁离子可诱导人牙髓细胞的增殖、分化和矿化，参与牙髓修复过程，在盖髓剂中引入镁离子被认为是促进牙组织再生的新途径[76-78]。同时，镁对牙体硬组织的矿化也十分重要，WON等[79]利用单细胞RT-PCR方法检测镁离子渗透性离子通道TRPM7和镁离子转运体CNNM4在大鼠成牙本质细胞中的表达，发现这2种分子可能是成牙本质细胞中主要的镁离子调节剂，CNNM4可能选择性参与根尖牙本质的形成或矿化。
2.3.5 镁及镁基材料作为药物负载材料的应用 目前，颌面部术后均有发生感染的风险，全身抗生素应用仍然是临床中最常用的预防及治疗方法，但该方法在感染部位可能无法达到足够的药物浓度。目前学者们通过实验使用可降解镁基材料制作了负载抗菌药物的局部给药系统，促进成骨及骨修复的同时成功克服了植入物周围血药浓度低的问题。BAKHSHESHI-RAD等[80]用新型空间保持器技术制备了负载强力霉素的镁-钙-TiO2复合支架，药物释放曲线显示出初始突释和持续释放2种模式，表现出明显的抑菌活性。也有学者发现，负载不同浓度四环素的镁锌合金支架可有效对抗金黄色葡萄球菌和大肠杆菌的活性，并且四环素浓度为1%-5%的镁锌支架能够更有效实现药物缓释，保证抗菌效果的长效性[81]。目前与镁基材料有关的药物负载局部给药系统的研究多集中于体外研究，鲜有有应用于体内的报道。
综上所述，镁基材料在颌面部及口内软组织再生、牙组织工程及药物负载中的应用大部分仍停留在体外实验阶段，仍需大量临床前期实验逐步向临床转化。目前的大多数研究将现有生物材料与镁基材料对比，未来可尝试将现有及临床使用成熟的生物材料与镁基材料联用，进一步拓展对镁基材料的应用。
2.4 生物安全性 目前，国内外对可降解金属植入物的生物学评价体系尚不完善。镁合金植入机体后降解太快，不能保持足够的稳定性，手术第1周内会出现机体不良反应，如局部肿胀和疼痛。因此，设计出耐腐蚀、生物相容性更稳定的镁基合金仍是一个亟待解决的问题[82-83]。等离子体电解氧化又称微弧氧化，是在传统阳极氧化基础上发展起来的一种环保的表面处理方法，可以在镁合金表面形成致密、厚实的陶瓷层。利用微弧氧化技术对镁基合金表面进行修饰，可提高合金的初始耐腐蚀性和机械强度，保护基材免受周围生物流体的伤害。另外，加入其他合金元素如稀土元素等可有效改善镁合金的力学性能、耐腐蚀性能和生物性能，但稀土元素不是人体必需的微量元素，过量可能会引起细胞毒性。对于不可降解金属的标准细胞毒性测试程序，即将金属放入培养液中一段时间，然后在该培养液中培养靶细胞以确定细胞毒性[84]。但这一标准不适用于可降解金属，因为它们会在培养基中发生降解，这是一个矛盾点。因此，建立并完善新的可降解金属体内外生物评价体系变得尤为重要。
2.2 镁及镁基材料的种类及生物学特性
2.2.1 镁及镁基材料的种类 2010年，镁及镁基材料在口腔医学上的应用研究开始大规模兴起，虽然临床研究较少，但仍有一定数量的体内外研究逐步开展。由于纯镁在机体内存在不稳定的生物学缺陷，学者们在纯镁中加入其他金属(如锌、锰、钇、铜等)制作镁基合金材料，以增强该类镁基合金材料的耐腐蚀性及生物相容性。常用于口腔医学领域体内研究的镁基金属如表2所示。
2.2.2 生物可降解性 镁及镁基材料植入后会在人体体液环境中发生降解，产生氢氧化镁、氢气和其他降解产物(图3)，其中氢氧化物会作为保护涂层附着于植入物表面，以防植入物进一步腐蚀降解[17]。人体内的巨噬细胞会吞噬部分降解产物，其余降解产物存留于骨基质中，储存在骨基质中的镁离子进一步与羟基磷灰石晶体结合，提高了羟基磷灰石晶体的溶解度，进而增加了骨强度[18]。在镁合金缓慢降解后，暂时积聚的镁离子可通过局部骨再生及循环系统释放，而不会引起血清镁离子水平的波动。正是由于这种生物可降解特性，当镁作为骨折固定物时避免了二次手术取出的风险。虽然纯镁在体内的降解产物无毒，降解产物镁离子等也能促进骨再生，但镁基植入物在体内降解过快容易导致骨折治疗失败，因此，提高镁合金植入物的耐腐蚀性是延长镁合金植入物体内固定时间的关键[19]。有研究表明，镁的降解伴随着镁离子和氢气的持续释放，增加材料表面微环境中pH值和渗透压，这些近表面效应也可能会影响残留的肿瘤细胞，具有潜在的抗肿瘤活性，如骨肉瘤的治疗[20]。
2.2.3 生物相容性 镁具有良好的生物相容性，植入后能与周围组织紧密接触且无不良反应，金属镁的密度为1.74-1.84 g/cm3，弹性模量为41-45 GPa，接近人体骨组织的密度和弹性模量(弹性模量为15-25 GPa)[21]，这些性能为镁及镁合金作为骨植入材料提供了良好的应用基础。另外，镁及镁合金降解产生的镁离子也不会对机体造成负担，因为细胞可以耐受比生理浓度大16倍的镁离子浓度。动物实验结果表明，经等离子体电解氧化锂的镁锌钙合金植入兔颅骨缺损部位后以2.32 mm/年的速率降解，没有引起兔的心、肝、肾、脾功能障碍[22]。在植入WE43镁螺钉植入治疗骨折的临床试验也未发现高镁血症的迹象，并且血中镁浓度水平正常[23]。在正颌手术患者中应用WE43镁压缩螺钉后未观察到过敏反应、肝肾功能障碍或镁血清水平升高等并发症[24]。
2.2.4 成骨特性 与传统骨内植入物(如钛、钛合金、钴铬合金)相比，镁是软组织和骨组织中的重要元素，参与许多生化反应。有研究建议健康成人每日摄入310-420 mg镁离子以维持正常的生命活动，储存24-30 g镁离子以维持基础代谢[25]。人体内的大部分镁离子储存在骨组织中，如果骨组织中的镁离子含量降低，骨组织的力学性能就会减弱，导致骨小梁断裂，增加骨折风险。即使过量的镁离子被摄入体内也可以迅速地通过循环和泌尿系统排出体外，不会造成任何损害[26]。DíAZ-TOCADOS等[27]研究证明，增加镁离子浓度可增强体外间充质干细胞的成骨作用，镁离子还通过激活Notch信号通路增强成碱性磷酸酶、Runx2、骨钙素mRNA的表达。HUNG等[28]研究发现，含10 mmol/L镁离子的细胞培养基可有效促进骨髓间充质干细胞的成骨分化，通过激活Wnt信号通路增加细胞外基质中的矿化和碱性磷酸酶表达。WANG等[29]研究证明，镁离子通过有丝分裂原活化蛋白激酶信号通路促进骨髓间充质干细胞中成骨分化标志物的表达，如骨形态发生蛋白2、Ⅰ型胶原蛋白、Runx2。有研究发现，镁提取物促进了小鼠胚胎成骨细胞前体细胞MC3T3-E1的增殖和血小板衍生生长因子分泌，从而促进了成骨细胞发育和骨形成[30]。此外，镁还促进脂肪源性基质细胞骨桥蛋白基因的表达，骨桥蛋白是早期生物材料细胞成骨相互作用的必需基因。镁离子能促进各种成骨细胞的成骨分化，这是镁应用于骨内金属植入物的基本理论依据。破骨细胞生成和成骨之间的双向平衡在骨再生中起着核心作用[31]。除了调节成骨细胞促进骨再生外，镁还可以抑制破骨细胞的生成和骨吸收[32]。
2.2.5 成血管性 对于颌面部组织重建而言，构建功能化的血管网络极其重要[33]。血管网络参与骨再生一般有膜内和软骨内骨化2种方式。在膜内骨化过程中，血管网络延伸到骨膜的间充质区域诱导分化出成骨细胞[34]；在软骨内骨化过程中，软骨模板中的非增殖软骨细胞分泌促血管生成因子以刺激血管生长，随着血管系统的扩张，软骨组织逐渐被骨组织取代，导致新骨的形成[35]。因此，促进体内血管化对骨再生至关重要。镁可调节多种内皮细胞的生物学功能，有研究表明，人脐静脉内皮细胞在一定量的镁离子中表现出高增殖率、良好的细胞形态和活力[36]。此外，一定浓度的镁离子也可以增加血管生成标志物的表达水平。YU等[10]采用等离子体浸没离子注入技术制备了一种潜在的牙种植体材料——双锌/镁离子共植入钛，以改善种植体的骨结合和长期生存，体外结果表明该系统中的镁离子通过上调人脐静脉内皮细胞中人镁离子转运蛋白的表达增加镁离子内流，通过激活缺氧诱导因子1α刺激血管内皮生长因子和血管内皮生长因子受体2的转录，从而诱导血管生成[37]。
2.2.6 免疫调节性 在骨组织工程中生物材料的骨免疫调节特性尤其受到重视，它影响着骨再生结果。免疫系统和骨骼系统共享着各种细胞因子受体和转录因子。巨噬细胞作为免疫系统的重要组成部分，包括M1型和M2型，M1型参与急性炎症，与组织修复的早期阶段密切相关；M2型在骨愈合后期发挥作用，导致主动修复或纤维组织的形成[38]。M1型和M2型巨噬细胞可以响应于各种生物材料而相互转换。巨噬细胞亚型转换过程可释放出各种成骨相关分子参与新骨形成。镁及镁基材料作为骨内金属植入物对成骨和破骨细胞有很大影响。当镁和镁合金植入体内后植入物周围的免疫反应会被触发，来自植入物的镁离子通过增强巨噬细胞向M2型极化来调节骨免疫微环境，M2型巨噬细胞分泌白细胞介素10以启动骨修复过程。此外，镁离子还可抑制M1巨噬细胞，降低促炎因子(肿瘤坏死因子α、白细胞介素6)的表达，从而起到抗炎作用。研究表明，镁合金植入后5 d和10 d显著刺激种植体-骨界面的巨噬细胞出现极化[39]。
综上所述，可降解镁基材料具有广泛的生物学活性，为其在口腔医学领域的临床应用奠定了基础。然而在免疫调节方面，目前研究仅集中于巨噬细胞所参与的组织反应，而对单核细胞、肥大细胞、T细胞和B细胞等的研究相对缺乏，以期日后进一步深入研究，完善相关免疫机制。同时，有部分学者提到的镁基材料抗肿瘤机制亦不清晰，相关详尽研究均待日后深入挖掘开展。
2.3 镁及镁基材料在口腔医学中的应用
2.3.1 镁及镁基材料在颌面部骨折中的应用 颌面部骨折大多由交通事故和暴力因素导致，对患者的外观容貌、言语和咀嚼功能都有显著影响。目前切开复位内固定是治疗颌面部骨折最常用的方法，使用的骨内固定材料多为不可降解金属，如广泛应用于临床的钛合金，尽管它具有良好的生物相容性、高耐磨性和高机械强度，但仍有一定的局限性，如可能发生暴露、感染、植入物松动及异物感等并发症，发生概率高达3%-25%[40]，并且通常还需要二次手术取出，额外的手术也无疑增加了患者的痛苦和经济负担。之后有学者发现可降解合成聚合物如聚乳酸和聚乙醇酸可作为骨内固定物使用，并解决上述问题。然而多项研究证实，合成聚合物降解可产生有毒的残留单体、磨损碎片和积累酸性中间产物，这些产物可能导致病理性骨吸收，并且这类合成聚合物的强度比钛合金弱得多，因此临床使用受到限制。纯镁在人体组织内可发生快速降解并产生氢气，不仅无法有效固定骨折断端，还可能引起周围组织气肿，但通过加入其他金属元素及表面改性技术可提高镁基合金的耐腐蚀性和生物相容性，有效解决这一问题[41-43]。
NAUJOKAT等[44]在小型猪实验中发现，WE43涂层镁合金固定面中部骨折取得了可喜效果，30周内未发生明显的降解。SCHALLER等[45]在猪眶上缘和颧骨面中截骨手术中使用WE43镁合金或聚乳酸-羟基乙酸植入物固定后，与合成聚合物聚乳酸-羟基乙酸植入物相比，镁合金具有更小的植入物尺寸和更高的机械性能，可在负载环境中支持骨折愈合。LEONHARDT等[46]与KOZAKIEWICZ等[47]对可降解镁基加压螺钉植入治疗下颌髁突骨折的临床随访观察显示，镁合金植入物固定1年后的下颌骨髁突骨质愈合良好，颞下颌关节活动度好，张口受限明显改善，虽螺钉周围显示有气体产生但无需取出。由于固定颌面部骨折时大多采用口内入路，这就要求用于颌面区域的可生物降解材料必须克服该区域特有的因素，包括附着于颌面部不同骨骼的咀嚼肌力量、唾液的特有生理环境和口腔内病原微生物的存在。镁基材料具有良好的机械强度和生物相容性，临床应用已得到证实。然而，镁基合金的抗压强度低于钛合金，这就限制了其在颌骨骨折特别是承重骨折中的应用[48]。下颌骨骨折是颌面部最常见的骨折类型，因有强大的升颌肌群和降颌肌群附着，常导致骨折块移位，咬合错乱，因此，下颌骨骨折的固定物要求有一定的机械性能。镁及镁基材料在颌面部骨折中的应用[49-53]，见表3。ORASSI等[51]通过有限元分析发现，镁合金钢板及螺钉在治疗4种下颌骨骨折类型中的固定性能表现与钛合金基本相同。ANSOMS等[52]研究显示，镁合金固定材料具有足够的机械性能承担下颌角骨折部分所承担的咀嚼力。随后有学者利用有限元分析模型模拟在正颌外科手术中使用WE43镁合金螺钉固定下颌升支矢状劈开截骨的骨折线，结果显示在咀嚼负载情况下WE43镁合金仍能稳定固定骨折线，打开了生物可降解镁合金在正颌外科方面应用的大门，提供了更多的可能性和研究方向[53-54]。
镁及镁基材料的临床应用，见表4。
2.3.2 镁及镁基材料在口腔骨再生领域中的应用
引导性骨再生技术：引导性骨再生技术中使用的引导性骨再生生物膜作为硬组织和软组织之间的屏障，可以防止软组织干扰成骨，从而为成骨细胞的分化提供足够空间，进而诱导成骨，治疗因牙周炎、拔牙、肿瘤或囊肿等疾病导致的骨缺损。临床使用的生物膜一类是可吸收的，例如合成聚合物聚乳酸-羟基乙酸、聚乙烯亚胺、聚(L-乳酸)或天然聚合物(胶原蛋白，壳聚糖)等；另一类是不可吸收的，例如钛网或聚四氟乙烯等[56]。目前临床广泛使用的胶原蛋白类可吸收生物膜虽具有良好的生物相容性与可降解性，但机械性能不足，在修复大面积及垂直性骨缺损时可能会塌陷，导致缺损部位成骨作用不足，而不可吸收类的钛网虽具有足够的机械性能，但可能需二次手术取出，应用也受到限制。多项体内外研究表明，采用热轧纯镁(镁95.5%)生物膜具有与胶原蛋白膜相当的成骨能力，并且具有良好的机械强度与缓慢降解特性，可以维持骨形成的空间，达到治疗骨高度不足及大面积骨缺损的目的[12-13]。FROSECCHI[57]将纯镁生物膜与胶原蛋白膜联合应用于治疗临床中牙槽骨的复杂骨缺损，取得了良好的成骨效果。也有学者采用不同表面处理方法提升了镁膜的免疫性及成骨性[57-61]，在降低镁膜降解率的同时也降低了骨组织细菌感染和骨吸收风险(表5)。
骨替代材料：通常同种骨、异种骨、异体骨及合成骨替代材料被用作移植材料用于颅颌面骨缺损的治疗，随着材料在医学领域的飞速发展，更多的合成材料被引入作为骨移植材料，包括钙磷陶瓷、生物玻璃及以聚乳酸为基础的可吸收聚合物。其中，钙磷陶瓷由于与骨组织的矿物组成和性质最接近而最受青睐[64]，主要以颗粒状羟基磷灰石、β-磷酸三钙盐或两者的混合物应用于临床治疗，如上颌窦底提升及拔牙后的位点保存技术[65]。但有研究证实颗粒状的磷酸钙材料也存在风险，比如可能由于其尖锐的颗粒状边缘引起上颌窦底黏膜穿孔，或者作为骨替代材料吸收率不佳，不能完全被骨组织所替代。与传统磷酸钙材料相比，镁基材料可以在中性pH值下发生化学反应产生鸟粪石(MgNH4PO4×?6H2O)等矿物，此类矿物在pH值7.01-9.62范围内具有比磷酸钙更好的吸收率，并且释放的镁离子可刺激骨骼重塑，展示出更好的溶解性和生物相容性[66]。同时，以磷酸镁为基础的镁基骨替代物大多是通过矿物粉末与水溶液混合胶凝反应加工得来，有学者通过在表面活性剂稳定的亲油性液体中乳化不同剂量比的钙镁磷水泥浆体，成功合成了具有理想尺寸分布的完全球形无创颗粒，进一步加速了镁基材料成为一种更理想骨替代材料的可能[67]。
2.3.3 镁及镁基材料在牙种植体表面涂层的应用 钛合金是牙种植体修复中应用最广泛的一种金属种植体，它可以为后期的全冠修复提供稳定基础。然而，由于纯钛种植体表面缺乏抗菌活性，种植体植入后为口腔内各种革兰阳性和阴性细菌的生长和入侵创造了良好环境，增加了感染风险，导致种植体松动[68]。因此，对钛种植体表面进行改性提高其抗菌活性、促进骨细胞附着，已成为目前解决上述问题的重要途径[69]。镁离子作为体内的重要元素参与骨愈合，通过调节体内L型钙通道降低细胞内钙浓度，可抑制种植体植入后活性氧的产生，以此减少炎症因子释放，进而发挥抗炎和抗氧化作用[70]；此外，镁离子可以随尿排泄，通过肾小管重吸收，具有良好的体内生物降解性。有体外研究结果表明，镁基涂层钛植入物可增强骨髓间充质干细胞的增殖、增加成骨标志物(碱性磷酸酶、骨钙素、骨桥蛋白、骨唾液蛋白、Runx2)的表达、增加Ⅰ型胶原沉积和抗菌活性，同时，镁离子通过调节血清钙、磷水平预防局部高钙、高磷，从而避免局部矿化，更好地促进骨愈合[71-73]。有学者将通过半粉末冶金技术将石墨烯纳米片和碳纳米管纳米系统作为增强体均匀分散在镁锌合金涂层的钛种植体中，可显著降低种植体外周的炎症反应和氧化应激，更好地抑制口腔中革兰阳性菌的生长，促进人牙龈成纤维细胞的增殖活性和成骨细胞的分化潜能，从而提高种植体的骨整合稳定性[74]。
2.3.4 镁及镁基材料在颌面部、口腔内软组织再生及牙组织工程中的应用 多项研究表明，镁及镁基材料在颌面部及口腔内软组织再生领域亦有良好的应用前景。镁对人成纤维细胞的迁移、黏附和口腔黏膜再生有积极作用。镁对成纤维细胞活性的影响可能对种植体表面改性和促进种植体颈部周围软组织愈合有良好影响。有研究表明，镁基金属植入物在降解过程中会释放出可溶的镁离子和氢气，具有神经保护和抗氧化作用[75]，中间产物镁石榴石B可通过磷脂酰肌醇3-激酶-蛋白激酶B信号转导促进神经干细胞分化、刺激局部神经再生、改善微循环，这与镁离子促进成骨的信号通路相吻。镁对神经疼痛的治疗有一定效果，补充镁对颌面部周围神经损伤的恢复也有效果，但镁在运动神经中的应用有待进一步研究。在牙组织工程方面，镁离子可诱导人牙髓细胞的增殖、分化和矿化，参与牙髓修复过程，在盖髓剂中引入镁离子被认为是促进牙组织再生的新途径[76-78]。同时，镁对牙体硬组织的矿化也十分重要，WON等[79]利用单细胞RT-PCR方法检测镁离子渗透性离子通道TRPM7和镁离子转运体CNNM4在大鼠成牙本质细胞中的表达，发现这2种分子可能是成牙本质细胞中主要的镁离子调节剂，CNNM4可能选择性参与根尖牙本质的形成或矿化。
2.3.5 镁及镁基材料作为药物负载材料的应用 目前，颌面部术后均有发生感染的风险，全身抗生素应用仍然是临床中最常用的预防及治疗方法，但该方法在感染部位可能无法达到足够的药物浓度。目前学者们通过实验使用可降解镁基材料制作了负载抗菌药物的局部给药系统，促进成骨及骨修复的同时成功克服了植入物周围血药浓度低的问题。BAKHSHESHI-RAD等[80]用新型空间保持器技术制备了负载强力霉素的镁-钙-TiO2复合支架，药物释放曲线显示出初始突释和持续释放2种模式，表现出明显的抑菌活性。也有学者发现，负载不同浓度四环素的镁锌合金支架可有效对抗金黄色葡萄球菌和大肠杆菌的活性，并且四环素浓度为1%-5%的镁锌支架能够更有效实现药物缓释，保证抗菌效果的长效性[81]。目前与镁基材料有关的药物负载局部给药系统的研究多集中于体外研究，鲜有有应用于体内的报道。
综上所述，镁基材料在颌面部及口内软组织再生、牙组织工程及药物负载中的应用大部分仍停留在体外实验阶段，仍需大量临床前期实验逐步向临床转化。目前的大多数研究将现有生物材料与镁基材料对比，未来可尝试将现有及临床使用成熟的生物材料与镁基材料联用，进一步拓展对镁基材料的应用。
2.4 生物安全性 目前，国内外对可降解金属植入物的生物学评价体系尚不完善。镁合金植入机体后降解太快，不能保持足够的稳定性，手术第1周内会出现机体不良反应，如局部肿胀和疼痛。因此，设计出耐腐蚀、生物相容性更稳定的镁基合金仍是一个亟待解决的问题[82-83]。等离子体电解氧化又称微弧氧化，是在传统阳极氧化基础上发展起来的一种环保的表面处理方法，可以在镁合金表面形成致密、厚实的陶瓷层。利用微弧氧化技术对镁基合金表面进行修饰，可提高合金的初始耐腐蚀性和机械强度，保护基材免受周围生物流体的伤害。另外，加入其他合金元素如稀土元素等可有效改善镁合金的力学性能、耐腐蚀性能和生物性能，但稀土元素不是人体必需的微量元素，过量可能会引起细胞毒性。对于不可降解金属的标准细胞毒性测试程序，即将金属放入培养液中一段时间，然后在该培养液中培养靶细胞以确定细胞毒性[84]。但这一标准不适用于可降解金属，因为它们会在培养基中发生降解，这是一个矛盾点。因此，建立并完善新的可降解金属体内外生物评价体系变得尤为重要。
| [1] VUJOVIĆ S, DESNICA J, STANIŠIĆ D, et al. Applications of biodegradable magnesium-based materials in reconstructive oral and maxillofacial surgery: a review. Molecules. 2022;27(17):5529. [2] XING F, LI S, YIN D, et al. Recent progress in Mg-based alloys as a novel bioabsorbable biomaterials for orthopedic applications. J Magnes Alloy. 2022; 10(6):1428-1456. [3] LI Y, WANG J, YUE J, et al. High magnesium prevents matrix vesicle‐mediated mineralization in human bone marrow‐derived mesenchymal stem cells via mitochondrial pathway and autophagy. Cell Biol Int. 2018;42(2):205-215. [4] HUSE EC. A New Ligature. Chic Med J Exam. 1878;37(2):171-172. [5] WITTE F. The history of biodegradable magnesium implants: a review. Acta Biomater. 2010;6(5):1680-1692. [6] MCBRIDE E. Magnesium screw and nail transfixion in fractures. South Med J. 1938;31:508-514. [7] EGGEBRECHT H, RODERMANN J, HUNOLD P, et al. Images in cardiovascular medicine. Novel magnetic resonance-compatible coronary stent: the absorbable magnesium-alloy stent. Circulation. 2005;112(18):e303-304. [8] ROJAEE R, FATHI M, RAEISSI K. Controlling the degradation rate of AZ91 magnesium alloy via sol-gel derived nanostructured hydroxyapatite coating. Mater Sci Eng C Mater Biol Appl. 2013;33(7):3817-3825. [9] SCHALLER B, SAULACIC N, BECK S, et al. In vivo degradation of a new concept of magnesium-based rivet-screws in the minipig mandibular bone. Mater Sci Eng C Mater Biol Appl. 2016;69:247-254. [10] YU Y, JIN G, XUE Y, et al. Multifunctions of dual Zn/Mg ion co-implanted titanium on osteogenesis, angiogenesis and bacteria inhibition for dental implants. Acta Biomater. 2017;49:590-603. [11] FUCHS A, KRECZY D, BRÜCKNER T, et al. Bone regeneration capacity of newly developed spherical magnesium phosphate cement granules. Clin Oral Investig. 2022;26(3):2619-2633. [12] RIDER P, KAČAREVIĆ Ž P, ELAD A, et al. Biodegradable magnesium barrier membrane used for guided bone regeneration in dental surgery. Bioact Mater. 2022;14:152-168. [13] RIDER P, KAČAREVIĆ ŽP, ELAD A, et al. Analysis of a pure magnesium membrane degradation process and its functionality when used in a guided bone regeneration model in beagle dogs. Materials. 2022;15(9):3106. [14] ZHAO Z, YU W, YANG W, et al. Dual-Protection Inorganic-Protein Coating on Mg-Based Biomaterials through Tooth-Enamel-Inspired Biomineralization. Adv Mater. 2024;36(21):e2313211. [15] BYUN SH, LIM HK, CHEON KH, et al. Biodegradable magnesium alloy (WE43) in bone-fixation plate and screw. J Biomed Mater Res B Appl Biomater. 2020; 108(6):2505-2512. [16] YANG GF, KIM YC, HAN HS, et al. In vitro dynamic degradation behavior of new magnesium alloy for orthopedic applications. J Biomed Mater Res B Appl Biomater. 2015;103(4):807-815. [17] AMUKARIMI S, MOZAFARI M. Biodegradable magnesium biomaterials—Road to the clinic. Bioengineering. 2022;9(3):107. [18] GE J, YANG C, WANG Y, et al. Comparison of different grafting materials for treatment of bone defect distal to the molar in canine. Clin Implant Dent Relat Res. 2018;20(4):444-454. [19] TSAO YT, SHIH YY, LIU YA, et al. Knockdown of SLC41A1 magnesium transporter promotes mineralization and attenuates magnesium inhibition during osteogenesis of mesenchymal stromal cells. Stem Cell Res Ther. 2017;8:1-10. [20] TORRONI A, XIANG C, WITEK L, et al. Biocompatibility and degradation properties of WE43 Mg alloys with and without heat treatment: In vivo evaluation and comparison in a cranial bone sheep model. J Craniomaxillofac Surg. 2017;45(12): 2075-2083. [21] WANG J, XU J, LIU W, et al. Biodegradable magnesium (Mg) implantation does not impose related metabolic disorders in rats with chronic renal failure. Sci Rep. 2016;6(1):26341. [22] BARBECK M, KÜHNEL L, WITTE F, et al. Degradation, bone regeneration and tissue response of an innovative volume stable magnesium-supported GBR/GTR barrier membrane. Int J Mol Sci. 2020;21(9):3098. [23] LIU Y, WANG DL, HUANG YC, et al. Hydrogen inhibits the osteoclastogenesis of mouse bone marrow mononuclear cells. Mater Sci Eng C Mater Biol Appl. 2020;110:110640. [24] MRAIED H, WANG W, CAI W. Influence of chemical heterogeneity and microstructure on the corrosion resistance of biodegradable WE43 magnesium alloys. J Mater Chem B. 2019;7(41):6399-6411. [25] PROBST FA, FLIEFEL R, BURIAN E, et al. Bone regeneration of minipig mandibular defect by adipose derived mesenchymal stem cells seeded tri-calcium phosphate-poly (D, L-lactide-co-glycolide) scaffolds. Sci Rep. 2020;10(1):2062. [26] JÄHN K, SAITO H, TAIPALEENMÄKI H, et al. Intramedullary Mg2Ag nails augment callus formation during fracture healing in mice. Acta Biomater. 2016;36:350-360. [27] DÍAZ-TOCADOS JM, HERENCIA C, MARTÍNEZ-MORENO JM, et al. Magnesium chloride promotes osteogenesis through Notch signaling activation and expansion of mesenchymal stem cells. Sci Rep. 2017;7(1):7839. [28] HUNG CC, CHAYA A, LIU K, et al. The role of magnesium ions in bone regeneration involves the canonical Wnt signaling pathway. Acta Biomater. 2019;98:246-255. [29] WANG Z, LIU Q, LIU C, et al. Mg2+ in β‐TCP/Mg–Zn composite enhances the differentiation of human bone marrow stromal cells into osteoblasts through MAPK‐regulated Runx2/Osx. J Cell Physiol. 2020;235(6):5182-5191. [30] GAO P, FAN B, YU X, et al. Biofunctional magnesium coated Ti6Al4V scaffold enhances osteogenesis and angiogenesis in vitro and in vivo for orthopedic application. Bioact Mater. 2020;5(3):680-693. [31] CECCHINATO F, KARLSSON J, FERRONI L, et al. Osteogenic potential of human adipose-derived stromal cells on 3-dimensional mesoporous TiO2 coating with magnesium impregnation. Mater Sci Eng C Mater Biol Appl. 2015;52:225-234. [32] EL-RASHIDY AA, ROETHER JA, HARHAUS L, et al. Regenerating bone with bioactive glass scaffolds: A review of in vivo studies in bone defect models. Acta Biomater. 2017;62:1-28. [33] BYAMBAA B, ANNABI N, YUE K, et al. Bioprinted osteogenic and vasculogenic patterns for engineering 3D bone tissue. Adv Healthc Mater. 2017;6(16):1700015. [34] PERCIVAL CJ, RICHTSMEIER JT. Angiogenesis and intramembranous osteogenesis. Dev Dyn. 2013;242(8):909-922. [35] DIRCKX N, VAN HUL M, MAES C. Osteoblast recruitment to sites of bone formation in skeletal development, homeostasis, and regeneration. Birth Defects Res C Embryo Today. 2013;99(3):170-191. [36] GU Y, ZHANG J, ZHANG X, et al. Three-dimensional printed Mg-doped β-TCP bone tissue engineering scaffolds: effects of magnesium ion concentration on osteogenesis and angiogenesis in vitro. Tissue Eng Regen Med. 2019;16:415-429. [37] MAU JR, HAWKINS KM, WOO SL, et al. Design of a new magnesium-based anterior cruciate ligament interference screw using finite element analysis. J Orthop Translat. 2020;20:25-30. [38] SADOWSKA JM, GINEBRA MP. Inflammation and biomaterials: role of the immune response in bone regeneration by inorganic scaffolds. J Mater Chem B. 2020;8(41):9404-9427. [39] RAHMATI M, STÖTZEL S, KHASSAWNA TE, et al. Early osteoimmunomodulatory effects of magnesium–calcium–zinc alloys. J Tissue Eng. 2021;12: 20417314211047100. [40] GLOBIG P, WILLUMEIT-RÖMER R, MARTINI F, et al. Optimizing an osteosarcoma-fibroblast coculture model to study antitumoral activity of magnesium-based biomaterials. Int J Mol Sci. 2020;21(14):5099. [41] MARUKAWA E, TAMAI M, TAKAHASHI Y, et al. Comparison of magnesium alloys and poly‐l‐lactide screws as degradable implants in a canine fracture model. J Biomed Mater Res B Appl Biomater. 2016;104(7):1282-1289. [42] BONITHON R, KAO AP, FERNÁNDEZ MP, et al. Multi-scale mechanical and morphological characterisation of sintered porous magnesium-based scaffolds for bone regeneration in critical-sized defects. Acta Biomater. 2021;127:338-352. [43] WITTE F, KAESE V, HAFERKAMP H, et al. In vivo corrosion of four magnesium alloys and the associated bone response. Biomaterials. 2005;26(17):3557-3563. [44] NAUJOKAT H, RUFF CB, KLÜTER T, et al. Influence of surface modifications on the degradation of standard-sized magnesium plates and healing of mandibular osteotomies in miniature pigs. Int J Oral Maxillofac Surg. 2020;49(2):272-283. [45] SCHALLER B, BURKHARD JPM, CHAGNON M, et al. Fracture healing and bone remodeling with human standard-sized magnesium versus polylactide–co-glycolide plate and screw systems using a mini-swine craniomaxillofacial osteotomy fixation model. J Oral Maxillofac Surg. 2018;76(10):2138-2150. [46] LEONHARDT H, ZIEGLER A, LAUER G, et al. Osteosynthesis of the mandibular condyle with magnesium-based biodegradable headless compression screws show good clinical results during a 1-year follow-up period. J Oral Maxillofac Surg. 2021;79(3):637-643. [47] KOZAKIEWICZ M, GABRYELCZAK I. Bone union quality after fracture fixation of mandibular head with compression magnesium screws. Materials. 2022;15(6): 2230. [48] MAO L, SHEN L, CHEN J, et al. Enhanced bioactivity of Mg–Nd–Zn–Zr alloy achieved with nanoscale MgF2 surface for vascular stent application. ACS Appl Mater Interfaces. 2015;7(9):5320-5330. [49] IMWINKELRIED T, BECK S, SCHALLER B. Pre-clinical testing of human size magnesium implants in miniature pigs: implant degradation and bone fracture healing at multiple implantation sites. Mater Sci Eng C Mater Biol Appl. 2020;108: 110389. [50] KOZAKIEWICZ M. Change in pull-out force during resorption of magnesium compression screws for osteosynthesis of mandibular condylar fractures. Materials. 2021;14(2):237. [51] ORASSI V, FISCHER H, DUDA GN, et al. In silico biomechanical evaluation of WE43 magnesium plates for mandibular fracture fixation. Front Bioeng Biotechnol. 2022;9:803103. [52] ANSOMS P, BARZEGARI M, VANDER SLOTEN J, et al. Coupling biomechanical models of implants with biodegradation models: A case study for biodegradable mandibular bone fixation plates. J Mech Behav Biomed Mater. 2023;147: 106120. [53] LEE JH, HAN HS, KIM YC, et al. Stability of biodegradable metal (Mg-Ca-Zn alloy) screws compared with absorbable polymer and titanium screws for sagittal split ramus osteotomy of the mandible using the finite element analysis model. J Craniomaxillofac Surg. 2017;45(10):1639-1646. [54] CHEN K, LU Y, TANG H, et al. Effect of strain on degradation behaviors of WE43, Fe and Zn wires. Acta Biomater. 2020;113:627-645. [55] KOZAKIEWICZ M, GABRYELCZAK I, BIELECKI-KOWALSKI B. Clinical evaluation of magnesium alloy osteosynthesis in the mandibular head. Materials. 2022; 15(3):711. [56] ELAD A, RIDER P, ROGGE S, et al. Application of biodegradable magnesium membrane shield technique for immediate dentoalveolar bone regeneration. Biomedicines. 2023;11(3):744. [57] FROSECCHI M. Horizontal and Vertical Defect Management with a Novel Degradable Pure Magnesium Guided Bone Regeneration (GBR) Membrane—A Clinical Case. Medicina. 2023;59(11):2009. [58] STEIGMANN L, JUNG O, KIEFERLE W, et al. Biocompatibility and immune response of a newly developed volume-stable magnesium-based barrier membrane in combination with a PVD coating for guided bone regeneration (GBR). Biomedicines. 2020;8(12):636. [59] KANNO T, SUKEGAWA S, FURUKI Y, et al. Overview of innovative advances in bioresorbable plate systems for oral and maxillofacial surgery. Jpn Dent Sci Rev. 2018;54(3):127-138. [60] WANG F, XIA D, WANG S, et al. Photocrosslinkable Col/PCL/Mg composite membrane providing spatiotemporal maintenance and positive osteogenetic effects during guided bone regeneration. Bioact Mater. 2022;13:53-63. [61] SHAN X, XU Y, KOLAWOLE SK, et al. Degradable pure magnesium used as a barrier film for oral bone regeneration. J Funct Biomater. 2022;13(4):298. [62] YAN ZY, ZHU JH, LIU GQ, et al. Feasibility and Efficacy of a Degradable Magnesium‐Alloy GBR Membrane for Bone Augmentation in a Distal Bone‐Defect Model in Beagle Dogs. Bioinorg Chem Appl. 2022;2022(1):4941635. [63] DONG Y, YAO L, CAI L, et al. Antimicrobial and pro-osteogenic coaxially electrospun magnesium oxide nanoparticles-polycaprolactone/parathyroid hormone-polycaprolactone composite barrier membrane for guided bone regeneration. Int J Nanomedicine. 2023;18:369-383. [64] FUCHS A, KRECZY D, BRÜCKNER T, et al. Bone regeneration capacity of newly developed spherical magnesium phosphate cement granules. Clin Oral Investig. 2022;26(3):2619-2633. [65] NABIYOUNI M, BRÜCKNER T, ZHOU H, et al. Magnesium-based bioceramics in orthopedic applications. Acta Biomater. 2018;66:23-43. [66] WANG N, MA Y, SHI H, et al. Mg-, Zn-, and Fe-based alloys with antibacterial properties as orthopedic implant materials. Front Bioeng Biotechnol. 2022;10:888084. [67] BLUM C, BRÜCKNER T, EWALD A, et al. Mg: Ca ratio as regulating factor for osteoclastic in vitro resorption of struvite biocements. Mater Sci Eng C Mater Biol Appl. 2017;73:111-119. [68] HERNÁNDEZ-ESCOBAR D, PAJARES-CHAMORRO N, CHATZISTAVROU X, et al. Tailored Coatings for Enhanced Performance of Zinc–Magnesium Alloys in Absorbable Implants. ACS Biomater Sci Eng. 2023;10(1):338-354. [69] BAI Y, WANG L, ZHAO L, et al. Antibacterial and Antioxidant Effects of Magnesium Alloy on Titanium Dental Implants. Comput Math Methods Med. 2022;2022(1):6537676. [70] WON S, HUH Y H, CHO LR, et al. Cellular response of human bone marrow derived mesenchymal stem cells to titanium surfaces implanted with calcium and magnesium ions. Tissue Eng Regen Med. 2017;14:123-131. [71] MIHAILESCU N, STAN GE, DUTA L, et al. Structural, compositional, mechanical characterization and biological assessment of bovine-derived hydroxyapatite coatings reinforced with MgF2 or MgO for implants functionalization. Mater Sci Eng C Mater Biol Appl. 2016;59:863-874. [72] ONDER S, CALIKOGLU-KOYUNCU AC, KAZMANLI K, et al. Magnesium doping on TiN coatings affects mesenchymal stem cell differentiation and proliferation positively in a dose-dependent manner. Biomed Mater Eng. 2018;29(4):427-438. [73] TAO ZS, ZHOU WS, HE XW, et al. A comparative study of zinc, magnesium, strontium-incorporated hydroxyapatite-coated titanium implants for osseointegration of osteopenic rats. Mater Sci Eng C Mater Biol Appl. 2016;62:226-232. [74] LIU JR, WANG XY, SABERI A, et al. The effect of Co-encapsulated GNPs-CNTs nanofillers on mechanical properties, degradation and antibacterial behavior of Mg-based composite. J Mech Behav Biomed Mater. 2023;138:105601. [75] ZHANG J, ZHANG B, ZHANG J, et al. Magnesium promotes the regeneration of the peripheral nerve. Front Cell Dev Biol. 2021;9:717854. [76] KONG YY, HU XL, ZHONG YQ, et al. Magnesium-enriched microenvironment promotes odontogenic differentiation in human dental pulp stem cells by activating ERK/BMP2/Smads signaling. Stem Cell Res Ther. 2019;10(1):378. [77] ZHENG JM, KONG YY, LI YY, et al. MagT1 regulated the odontogenic differentiation of BMMSCs induced byTGC-CM via ERK signaling pathway. Stem Cell Res Ther. 2019;10(1):48. [78] SALEM RM, ZHANG C, CHOU LS. Effect of magnesium on dentinogenesis of human dental pulp cells. Int J Biomater. 2021;2021:6567455. [79] WON J, KIM JH, OH SB. Molecular expression of Mg2+ regulator TRPM7 and CNNM4 in rat odontoblasts. Arch Oral Biol. 2018;96:182-188. [80] BAKHSHESHI-RAD HR, HAMZAH E, STAIGER MP, et al. Drug release, cytocompatibility, bioactivity, and antibacterial activity of doxycycline loaded Mg-Ca-TiO2 composite scaffold. Mater Des. 2018;139:212-221. [81] DAYAGHI E, BAKHSHESHI-RAD HR, HAMZAH E, et al. Magnesium-zinc scaffold loaded with tetracycline for tissue engineering application: in vitro cell biology and antibacterial activity assessment. Mater Sci Eng C Mater Biol Appl. 2019;102:53-65. [82] KIM SR, LEE KM, KIM JH, et al. Biocompatibility evaluation of peo-treated magnesium alloy implants placed in rabbit femur condyle notches and paravertebral muscles. Biomater Res. 2022;26(1):29. [83] ZHAO Z, YU W, YANG W, et al. Dual‐Protection Inorganic‐Protein Coating on Mg-Based Biomaterials through Tooth-Ename-Inspired Biomineralization. Adv Mater. 2024;36(21):e2313211. [84] KLÍMA K, ULMANN D, BARTOŠ M, et al. A complex evaluation of the in-vivo biocompatibility and degradation of an extruded ZnMgSr absorbable alloy implanted into rabbit bones for 360 days. Int J Mol Sci. 2021;22(24):13444. |
| [1] | 赵 帅, 李冬瑶, 魏岁艳, 曹怡静, 许 燕, 徐国强. 静电纺丝聚偏氟乙烯压电仿生骨膜的生物相容性评价[J]. 中国组织工程研究, 2025, 29(4): 730-737. |
| [2] | 刘 璐, 钟 畅, 余 欣, 任晨媛, 巩杨杨, 周 平, 王迎斌. 体外合成微环境促进人多能干细胞来源心肌细胞成熟的学术进展及临床应用[J]. 中国组织工程研究, 2025, 29(36): 7856-7862. |
| [3] | 王景帅, 张晓彤, 张彦歌, 万泽东, 孔令伟, 曹海营, 金 宇. Mg-Li-Gd合金与不锈钢髓内针植入固定大鼠股骨环形半缺损的比较[J]. 中国组织工程研究, 2025, 29(34): 7261-7268. |
| [4] | 李若彤, 吴悦宁, 邓云艺, 陈世超, 兰小蓉, 李适廷, 李广文. 聚多巴胺修饰还原石墨烯负载纳米银复合Gap19多肽水凝胶的制备及抗菌评价[J]. 中国组织工程研究, 2025, 29(34): 7333-7343. |
| [5] | 吴子炜, 罗诒财, 韦银格, 廖红兵. 聚乳酸-羟基乙酸共聚物在口腔医学领域的应用[J]. 中国组织工程研究, 2025, 29(34): 7393-7404. |
| [6] | 马毓聪, 欧阳峥峥, 刘小杰, 杨思飞. 医用镁合金材料研究趋势与热点追踪[J]. 中国组织工程研究, 2025, 29(34): 7470-7480. |
| [7] | 石纯熔, 何家旭, 邓丽姗, 王海蓝, 赵爱敏, 于沂灵, 耿海霞, 宋卫军. 氧化石墨烯在口腔种植修复领域的应用[J]. 中国组织工程研究, 2025, 29(28): 6118-6126. |
| [8] | 吴正敏, 李常旭, 崔艳玮, 陈 溯. 下颌All-on-4种植固定义齿不同咬合接触应力分布的有限元分析[J]. 中国组织工程研究, 2025, 29(28): 6020-6029. |
| [9] | 樊佳兵, 付雪飞, 张军梅, 周索頔, 莫朝伦. 3D打印导板引导正畸微种植钉植入的精确性[J]. 中国组织工程研究, 2025, 29(24): 5102-5108. |
| [10] | 彭璐瑶, 顾 瑜. 硒及硒纳米颗粒生物学机制与口腔常见疾病的关系[J]. 中国组织工程研究, 2025, 29(22): 4813-4822. |
| [11] | 宋雨菲, 程焕芝, 范海霞, 侯 萌. 3D打印技术在口腔医学、颌面外科修复重建中的作用与优势[J]. 中国组织工程研究, 2025, 29(22): 4823-4831. |
| [12] | 杨文静, 格根塔娜. 有限元分析牙髓根尖周病根管治疗中的牙体力学性能[J]. 中国组织工程研究, 2025, 29(20): 4295-4304. |
| [13] | 薛广明, 木合塔尔·克力木, 李 洪. 新型混编支架的制备与径向支撑力学行为[J]. 中国组织工程研究, 2025, 29(16): 3440-3448. |
| [14] | 胡张捷, 张宝贯, 张智武. 固态胶原基材料在医疗器械中的应用[J]. 中国组织工程研究, 2025, 29(16): 3503-3512. |
| [15] | 李志超, 杨振国, 王 磊, 王文波, 薛景才, 刘文斌, 曹 慧. 外泌体来源非编码RNA对骨关节炎微环境的作用及临床应用进展[J]. 中国组织工程研究, 2025, 29(13): 2784-2792. |
镁被认为是21世纪最好的绿色金属材料，是人体内的第四大阳离子元素，参与了300多种细胞酶促反应、线粒体活性、蛋白质翻译、DNA合成和细胞增殖[1]。健康成人体内约60%的镁沉积在骨骼中，镁从肠道被吸收，其在机体内的稳态依赖于肾功能。由于镁的力学性能和弹性模量与人类骨骼相似，表现出良好的生物安全性。从19世纪开始，以镁合金为代表的新型生物可降解金属发展迅速，凭借生物可降解性、机械性能、促成骨能力、生物相容性和抗菌性能，已被广泛应用于组织再生和重建等医学领域[2]。镁基材料是指以镁和镁合金作为基底，与一种或几种金属及非金属人工结合而成的复合金属材料，这种复合金属材料打破了将生物惰性金属材料作为重建组织植入物的传统治疗方法[3]，利用镁基金属可在人体环境内降解的特性，达到金属植入物在起到组织重建作用后自行消失的目的。近年来，越来越多的研究将生物可降解镁基材料应用于口腔疾病领域，包括颌面部骨折固定、引导性组织再生术、牙种植体表面技术、口内软组织再生及牙组织工程等。该文在阐述生物可降解镁基材料作用及机制的基础上，对镁基材料在口腔疾病领域的应用进展进行综述，以期为扩展镁在口腔疾病领域的应用、发展及优化提供借鉴与参考。
中国组织工程研究杂志出版内容重点：生物材料；骨生物材料；口腔生物材料；纳米材料；缓释材料；材料相容性；组织工程
1.1 资料来源
1.1.1 检索人及检索时间 由第一作者在2024年5月进行检索。
1.1.2 文献检索时限 各数据库建库至2024年5月。
1.1.3 检索数据库 Web of Science、PubMed、中国知网和万方数据库。
1.1.4 检索词 以“镁，镁合金，镁基金属，骨折，种植，修复，牙髓，牙周炎，牙周疾病，囊肿，口腔癌”为中文检索关键词，以“magnesium，magnesium-based alloy，fracture，facial bone fractures，denture，dental implant，restorative dentistry，pulpitis，periodontitis，periodontal diseases，oral cancer”为英文检索关键词。
1.1.5 检索文献类型 研究原著、综述及荟萃分析。
1.1.6 手工检索情况 无。
1.2 入组标准
1.2.1 纳入标准 根据文章题目及摘要进行初步筛选，通过文献泛读和精读后提炼出与文章相关的研究原著、综述及荟萃分析。
1.2.2 排除标准 排除研究目的及内容与该文无关、重复性及陈旧性的文献。
1.1.1 检索人及检索时间 由第一作者在2024年5月进行检索。
1.1.2 文献检索时限 各数据库建库至2024年5月。
1.1.3 检索数据库 Web of Science、PubMed、中国知网和万方数据库。
1.1.4 检索词 以“镁，镁合金，镁基金属，骨折，种植，修复，牙髓，牙周炎，牙周疾病，囊肿，口腔癌”为中文检索关键词，以“magnesium，magnesium-based alloy，fracture，facial bone fractures，denture，dental implant，restorative dentistry，pulpitis，periodontitis，periodontal diseases，oral cancer”为英文检索关键词。
1.1.5 检索文献类型 研究原著、综述及荟萃分析。
1.1.6 手工检索情况 无。
1.1.7 检索策略 以PubMed数据库检索策略为例，见图1。
1.2 入组标准
1.2.1 纳入标准 根据文章题目及摘要进行初步筛选，通过文献泛读和精读后提炼出与文章相关的研究原著、综述及荟萃分析。
1.2.2 排除标准 排除研究目的及内容与该文无关、重复性及陈旧性的文献。
1.3 质量评估 共检索得到765篇文献，根据标题与摘要进行筛选，排除重复、内容不相关及年代较久远的文献，最终纳入84篇文献进行综述。文献筛选流程见图2。
3.1 既往他人在该领域研究的贡献和存在的问题 镁及镁基金属为新型生物可降解金属，由于优越的机械性能、促成骨能力、生物相容性和抗菌性能在口腔医学疾病治疗领域具有广泛的应用前景。目前，已有部分综述对镁的物理及生物性能进行阐述，但鲜有文章对镁在口腔医学领域的应用进行归纳总结；此外，目前的研究多关注于镁的可降解性及促成骨特性，对其促成血管特性及免疫调节性关注较少。针对镁在口腔医学各领域的应用大部分仍停留于实验阶段，临床应用鲜见相关报道，未来仍需长期的动物及临床试验。
3.2 该综述区别于他人他篇的特点 该文对镁及镁基材料的各项性能进行详细总结归纳，尤其是他人阐述较少的促成血管性及免疫调节性，着眼于镁的生物学特性与口腔医学的联系，归纳总结出镁在颌面部骨折、骨再生领域、牙种植体表面涂层、颌面部软组织再生及牙组织工程方面的应用，详细罗列动物实验及相关临床研究，具有较好的参考意义，为镁基材料的临床研究提供依据，希望能帮助研究人员在该领域继续探索。
3.3 该综述的局限性 该综述亦存在一定的局限性：有相关综述阐述了镁与其聚合物在软骨再生方面的作用，可能对颞下颌关节病治疗产生积极作用，但在该领域研究报道较少，因此，该文未对镁在颞下颌关节软骨治疗方面的应用进行概述；现有部分研究仍停留在动物实验阶段，镁的临床有效性仍需大量研究验证。
3.4 该综述的意义 该文对镁及镁基材料在口腔医学领域的应用进行综述，阐述了镁及镁基材料作为新型可降解材料在口腔医学乃至整个医学领域具有巨大的发展潜力，为进一步优化及推进镁基材料的临床应用进程提供了思路与参考，也为开拓镁基材料在口腔医学领域的应用范围奠定基础。中国是世界上镁资源最丰富的国家之一，镁及镁基材料的高效合理应用必将为中国口腔医学、组织工程及医学材料等多学科的发展打开新世界的大门。 中国组织工程研究杂志出版内容重点：生物材料；骨生物材料；口腔生物材料；纳米材料；缓释材料；材料相容性；组织工程
3.2 该综述区别于他人他篇的特点 该文对镁及镁基材料的各项性能进行详细总结归纳，尤其是他人阐述较少的促成血管性及免疫调节性，着眼于镁的生物学特性与口腔医学的联系，归纳总结出镁在颌面部骨折、骨再生领域、牙种植体表面涂层、颌面部软组织再生及牙组织工程方面的应用，详细罗列动物实验及相关临床研究，具有较好的参考意义，为镁基材料的临床研究提供依据，希望能帮助研究人员在该领域继续探索。
3.3 该综述的局限性 该综述亦存在一定的局限性：有相关综述阐述了镁与其聚合物在软骨再生方面的作用，可能对颞下颌关节病治疗产生积极作用，但在该领域研究报道较少，因此，该文未对镁在颞下颌关节软骨治疗方面的应用进行概述；现有部分研究仍停留在动物实验阶段，镁的临床有效性仍需大量研究验证。
3.4 该综述的意义 该文对镁及镁基材料在口腔医学领域的应用进行综述，阐述了镁及镁基材料作为新型可降解材料在口腔医学乃至整个医学领域具有巨大的发展潜力，为进一步优化及推进镁基材料的临床应用进程提供了思路与参考，也为开拓镁基材料在口腔医学领域的应用范围奠定基础。中国是世界上镁资源最丰富的国家之一，镁及镁基材料的高效合理应用必将为中国口腔医学、组织工程及医学材料等多学科的发展打开新世界的大门。 中国组织工程研究杂志出版内容重点：生物材料；骨生物材料；口腔生物材料；纳米材料；缓释材料；材料相容性；组织工程
#br#
文题释义：
镁：是地壳中第八丰富的元素，约占总质量的2%，是在自然界中分布最广的十大元素之一，被称为“碱土金属”。镁及镁基材料在口腔疾病领域不仅具有可降解性，还具有成骨、成血管、免疫调节等多种作用。活性氧：为细胞正常代谢的副产物，氧的部分还原代谢产物，具有强氧化能力。低浓度活性氧发挥复杂的信号传导功能，但当细胞产生的活性氧超过其抗氧化能力时可能会对细胞大分子(如脂质、蛋白质和 DNA)造成损害，导致氧化应激状态。
镁被认为是21世纪最好的绿色金属材料，镁基材料是指以镁和镁合金作为基底，与一种或几种金属及非金属人工结合而成的复合金属材料。在医学领域，这种复合金属材料打破了将生物惰性金属材料作为重建组织植入物的传统治疗方法[3]，近年来，生物可降解镁基材料广泛应用于口腔疾病领域，包括颌面部骨折固定、引导性组织再生术、牙种植体表面技术、口内软组织再生及牙组织工程等。该文对镁及镁基材料的各项性能进行详细总结归纳，尤其是他人阐述较少的成血管性及免疫调节性，着眼于镁的生物学特性与口腔医学的联系，归纳总结出镁在口腔医学领域的应用，详细罗列动物实验及相关临床研究，具有较好的参考意义，为镁基材料的临床研究提供依据。