HAF/YSZ梯度复合涂层的制备及结构和性能

李素敏1，张  芹2，赵玉涛1，笪祖林1，刘晓燕1，张  钊1   

  1. 1江苏大学材料科学与工程学院，江苏省镇江市 212013
    2江苏大学附属人民医院，江苏省镇江市 212013
  • 收稿日期:2011-08-17 修回日期:2011-10-06 出版日期:2011-11-19 发布日期:2011-11-19
  • 作者简介:李素敏☆，女，1977年生，山东省东明县人，汉族，江苏大学在读博士，讲师，主要从事生物医用材料、高分子基复合材料等研究。 li_sm@ ujs.edu.cn
  • 基金资助:

    江苏省自然科学基金项目(BK2003051)，江苏省复合材料工程技术研究中心研发项目(BM2003014)。

Preparation, structure and properties of HAF/YSZ gradient composite coatings

Li Su-min1, Zhang Qin2, Zhao Yu-tao1, Da Zu-lin1, Liu Xiao-yan1, Zhang Zhao1   

  1. 1School of Materials Science and Engineering, Jiangsu University, Zhenjiang  212013, Jiangsu Province, China
    2Affiliated People’s Hospital of Jiangsu University, Zhenjiang  212013, Jiangsu Province, China
  • Received:2011-08-17 Revised:2011-10-06 Online:2011-11-19 Published:2011-11-19
  • About author:Li Su-min☆, Studying for doctorate, Lecturer, School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu Province, China li_sm@ujs.edu.cn
  • Supported by:

    Natural Science Foundation of Jiangsu Province, No. BK2003051*; Project of Composite Materials Engineering and Technology Research Center of Jiangsu Province, No. BM2003014*

PDF

604

被引次数

11

摘要：

背景：在钛合金基体表面制备涂层的方法多为等离子喷涂法、溶胶-凝胶法、离子束溅射法等，所制备的涂层性能不稳定、成分单一，且涂层物相组成较难控制。
目的：采用射频磁控溅射技术在Ti6Al4V基体上制备含氟羟基磷灰石梯度复合涂层HAF/YSZ。
方法：在Ti6Al4V基体上以射频磁控溅射技术制备含氟羟基磷灰石梯度复合涂层HAF/YSZ，利用X射线光电子能谱、扫描电镜等对涂层的成分分布、形貌、界面结合进行表征。通过模拟体液实验分析和评价HAF/YSZ涂层、HAF1.2涂层及羟基磷灰石涂层的生物性能。
结果与结论：所制备的HAF/YSZ梯度涂层表面粗糙，呈多孔岛状结构，有利于新生骨组织生长；涂层与基体结合紧密，各层间相互扩散，整体一致性较好；经模拟体液浸泡后，涂层表面有新生物质沉积，表现出较好的生物活性及稳定性，且梯度复合涂层较氟含量单一的氟羟基磷灰石涂层具有更好的抗体液溶解能力及稳定性。

关键词: 梯度复合涂层, 钛合金, 氟羟基磷灰石, 磁控溅射, 模拟体液

Abstract:

BACKGROUND: Plasma spraying, sol-gel coating process and ion beam sputtering are often used for making coatings on the surface of titanium alloy, but the properties of the coatings are unstable, the composition is homogeneous, and the control of the phase composition is difficult.
OBJECTIVE: To prepare HAF/YSZ gradient composite coatings on Ti6Al4V substrate by radio frequency magnetron sputtering.
METHODS: The HAF/YSZ gradient composite coatings were deposited on Ti6Al4V substrate by radio frequency magnetron sputtering. X-ray photoelectron spectrum, electron probe, and scanning electron microscope were used to investigate the composition distribution, surface morphology and interface morphology of the coatings. The biological activity and stability of HAF/YSZ coatings, HAF1.2 coatings and HA coatings were analyzed and evaluated in siulated body fluid.
RESULTS AND CONCLUSION: The prepared HAF/YSZ gradient coatings could provide well grow conditions for fresh osseous tissue based on their porous structure and rough surface. The interface was closely combined with the coatings. Interdiffusion existed between layers, and the overall consistency was better. New substances deposited on the surfaces after immersing in siulated body fluid, which showed better biological activity and stability of HAF/YSZ gradient coatings. The anti-solubility and stability of HAF/YSZ coatings were better than that of single fluorine content coatings.