Chinese Journal of Tissue Engineering Research ›› 2013, Vol. 17 ›› Issue (34): 6183-6192.doi: 10.3969/j.issn.2095-4344.2013.34.019
Previous Articles Next Articles
Chen Bao-lin1, Wang Dong-an2, 3
Online:
2013-08-20
Published:
2013-08-20
About author:
Chen Bao-lin, Professor, Bureau of Scientific Research, Hulunbuir College, Hulunbeier 021008, Inner Mongolia Autonomous Region, China
baolinchenkyc@sina.com
CLC Number:
Chen Bao-lin, Wang Dong-an. Surface construction and biocompatibility of polymeric used for cardiovascular medical device[J]. Chinese Journal of Tissue Engineering Research, 2013, 17(34): 6183-6192.
Type and application of polymeric biomaterials used for cardiovascular medicine The type and application of polymeric biomaterials used for cardiovascular medicine showed [18-35] . Design requirements (parameters) of cardiovascular medical devices and implantable soft tissue substitutes The design requirements based on the material angles should be considered from nine aspects (the first four aspects were mechanical properties) [36-42] : Strength The materials used for large arteries, heart valves and vascular balloon molding required high strength, such as the engineering plastics and synthetic compounds; materials of intervention catheters, surgical suture and intravascular stent should have moderate intensity, mainly included plastics, elastomers and various bions-derived materials; non-load bearing and weak shear surface coating materials required lower strength, the materials were mainly some biological macromolecules and hydrogels. In addition, the substrates of long-term interventional catheters and artificial blood vessels should had both strength and flexibility, the strength could ensure the completion of insert and torque actions, while the flexibility was intended to ensure not to damage the blood vessel wall and other bios tissues during the long-term application. Compliance (adaptability) The long-term interventional catheters, cardiac and vascular prostheses and artificial blood vessel materials required the compliance above average. Blood disorders usually occurred on the healing site of the arteries with relatively good compliance and the non-extendible grafts. The blood disorder could cause the changes in vascular permeability, and lead to anastomotic pseudoaneurysm intimal hyperplasia. Fiber shaping responses of elastomer were the reasons to the decreasing compliance of elastomer in the grafts within a certain time. On the other hand, even in the match compliance condition, there was a complex problem to be solved, that was the presence of excessive compliance region in the healing site, where there were likely to occur pseudoaneurysm. Creep resistance Creep resistance was used to measure the ability of the materials to maintain the shape and size under stress. The bios materials achieved the creep resistance through various forms of crosslinking. Among the synthetic materials, the cross-linked polymers (silicones) and multiphase block copolymers (polyurethane) also had good creep resistance; while the fluoropolymers, such as polytetrafluoroethylene, and uncrosslinked hydrogel had poor creep resistance. Aging resistance Aging resistance specifically referred to the ability of anti-progressive cracking of materials under critical stress and relaxation conditions. Most plastics had poor aging resistance, but polyether polyurethane elastomer had quite excellent aging resistance, and therefore widely used in cardiovascular medicine. Smoothness The surface smoothness of materials mainly reflected in the surface friction coefficient, which was essential for the interventional catheter, as the non-sufficiently smooth surface will seriously damaged the vessel wall. The surface smoothness of the materials were obtained mainly depend on the hydrogels or biopolymer surface coatings. Water absorption The strong water absorption of polymer material may easily lead adverse effects on the strength and creep resistance. The strength and other mechanical properties of nylon 6/6 were significantly reduced under moist conditions. Biological stability The biological stability of the materials could reflect the capabilities of resistance to degradation and maintaining in situ performance under application conditions. The forms that caused polymer degradation and performance loss reduction included hydrolysis, oxidation, hydrolysis, lipid deposition, swelling and calcification. Polyester polyurethane was easily hydrolyzed, polyether was easy to be oxidized, and the polyether polyurethane and silicone were prone to result in loss of material properties after absorbing esters substances. Calcification and digestion mainly occurs in the natural polymer materials and their derivatives under blood environment. Biological activity Biological activity mainly refers to the special material properties of some materials that are inherent and can participate in some bios reactions. For example, the bioactive coating materials can prevent blood coagulation or dissolute formed thrombus at the molecular level; negatively charged surfaces can eliminate the complement components on the interface; while the surface immobilized polypeptide or protein can promote the endothelial cell seeding and the bios soft tissue attachment on the surface of the materials. Biological responsiveness Biological responsiveness of the materials (such as inflammatory response and coagulation reaction) is an important indicator that should be considered in the biomaterial designing. The initial reaction of inflammatory response and coagulation response was originated in the interactions between proteins and cells on the surface of biomaterials. The chronic inflammatory response on the surface of biomaterials will lead to tissue fibrosis and long-term persistence of leukocytes on the inflammation sites, which can cause the necrosis of surrounding tissue and thus result in the failure of medical devices implantation. The implants suffered with environmental erosion, as well as the residual monomer, plasticizers, processing aids and degradation products in the materials may lead malignant allergic phenomena. Except for the coagulation and endogenous inflammatory response, pathogens as well as the endotoxin and body fragments will also lead to severe exogenous inflammatory responses, and the thrombus structure on the surface of biomaterials may also be the lesions of pathogen infection. In addition, angioplasty-caused intimal hyperplasia reaction will largely limit the application of small-diameter artificial blood vessels. Graft copolymer surface/block copolymer surfactant that can be used as biomaterials Compose of homopolymers and random copolymers are relatively homogeneous. Due to the influence of surface orientation effects, oxidation and pollution, chemical properties and the noumenon properties on the outermost layer of the materials are essentially different. However, for the graft copolymers and block copolymers, the difference between the surface and the noumenon will be reflected in many molecular layers that extending from the surface to the noumenon[43-48] . The two main factors determined the noumenon/surface behavior including noumenon/surface difference and surface phase separation, namely surface energy and molecular motion. Any interface tends to reach the state with the lowest interface energy, therefore, if there exits more than one component in one system, the component that lead to the lowest interface energy will be shifted to the surface as far as possible. Therefore, the polymer/air interface, the minimum surface energy components (or lowest surface energy functional groups) will be enriched in the interface layer. While in polymer/water interface, the maximum polar components and functional groups will be shifted to the interface to the maximum extent. The movement degree of the polymer molecules is directly related to the realization or not of the lowest interfacial energy mentioned above, if the molecular motion is limited, the energy minimization process of surface structure will be frozen in place. Thus, melting, dissolving solvent, heating above Tg and plasticizing treatment will contribute to realize the thermodynamically stable state to the maximum extent. If taking the difference of noumenon-surface composition into consideration, another additional determinant should be added, namely crystallization behavior of each component. If one of the components in the graft copolymer or block copolymer containing a relatively high crystallinity, the other components will be squeezed out, thus resulting in the surface regionalization. Crystalline can hind the molecular motion and diffusion. Finally, the incompatible degree of the two components of copolymers will affect phase separation tendency in the noumenon and surface layer. Graft copolymer surface Most of the researches on the graft copolymer surface focused on the characterization of polymer branch presented on the surface. The testing methods are mainly the surface infrared spectroscopy[49-52 ] , contact angle and X-ray photoelectron spectroscopy[52-54] . X-ray photoelectron spectroscopy is the common method to characterize the existence of surface grafting and quantitatively test the surface content, with the example of low density polyethylene grafted with poly (2-hydroxyethyl methacrylate). In view of the low grafting rate, the hydrometer method has been unable to provide accurate measurements, while XPS is able to meet the requirements[54-56] . The principle of minimum interfacial energy has a very important manifestation in the graft copolymer system. When testing the silicone rubber of radiation grafting hydrogels by XPS photoelectron spectroscopy under hydration state (-160 ℃), the corresponding graft tile peak will be reflected on the Si peak[57] . While after sample dehydration (in situ processing to make the sample temperature increase to the room temperature in the X-ray photoelectron spectroscopy devices), there is almost no spectral peaks of graft components. As the sampling depth of X-ray photoelectron spectroscopy was about 100 A, we can find that the detected surface structure reconstruction is based on the multilayer molecular scale. Similar surface chemistry changes can be found in comb copolymer containing pro-hydrophobic segments, such as the poly(2-hydroxyethyl methacrylate) [58] . Due to the different nature of the interface during annealing, its pro-hydrophobicity can be significantly adjusted. For example, if annealing on Teflon or in air, the hydrophobic surface could be obtained; if annealing on the polarity Mylar surface, the water infiltration surface will be obtained. Many literatures have reported the changes in surface chemistry caused by interfacial properties and environmental factors[57, 59-63] . The driving force of such changes was initially thought to be based on the energy changing, that is the decreasing surface energy. However, recent studies showed the dilution effect of noumenon based on entropy change properties on the surface functional groups could be considered as the driving force to the chemical changes above, and then acted on some certain solution system. For example, characterized with polyethylene exposed to N2RF-induced plasma coupling system by X-ray photoelectron spectroscopy will found that the surface content of nitrogen containing functional groups was reduced due to the presence of solvent, and the reason was the presence of solvent destructed the hydrogen bonds between chains. And for hydrogen bonds, the non-covalently bonded crosslink form, can reduce the movement of molecules, and thus limiting the surface functional groups to diffuse to the noumenon. In some recent experiments on radiation grafting, two different monomers were grafted on the same substrate simultaneously, thus getting in-depth observation on the complex surface systems[64]. In the experiments, hydroxyethylmethacrylate and poly(2-hydroxyethylmethacrylate) were grafted on low-density polyethylene surface with irradiation method. The products of the experiments were characterized with X-ray photoelectron spectroscopy, and the results showed the hydroxyethylmethacrylate firstly, and then the poly(2-hydroxyethylmethacrylate), which strongly determined the nature of the product surface. Indicating that no matter the copolymerization product obtained by simple solution, or the “normal” graft copolymerization product, the surface of the products was not the balance system. Studies on the surface area of a single compound were carried out based on the idea above. The surface grafted sample with radio frequency plasma deposition has aroused widespread interest due to its unique chemical properties. The in-depth characterization indicates that the unique chemical properties are derived from atomic sequences rearrangement, namely that the monomer molecules can split into several charged radical fragments in the plasma environment. The rearrangement of these fragments in the radio frequency plasma reactor and the deposition based on any surface can be achieved by a complex behavior. The conduction of this behavior is determined by the monomer concentration, plasma radiation intensity, accurate stoichiometric reaction and the presence of second component with accelerating or delaying reactions, as well as the ratio of surface etching rate to surface deposition rate. There are many reports on the preparation and properties of plasma-derived membrane[65-67] . The key of plasma-derived membrane is the significant boundaries exit in its component regions: graft chain-substrate interface, the commonly interface between plasma-derived membrane and the substrate, and the thickness is just about few molecules in terms of many such systems. It is different from the graft copolymer surface prepared with chemistry and radiation technology, as for the graft copolymer surface prepared with chemistry and radiation technology, the interface between the graft and noumenon has a few hundred to several thousand angstroms of gradient range[68-69] . Transmission electron microscopy and scanning electron microscopy can also get a lot of interesting information. The ultrathin section transmission electron microscopy image of the graft copolymer section can be used to characterize the morphology of graft chain and the substrate interface, as well as the morphology of surface region of the materials. In the preparation process of transmission electron microscopy samples, cutting, staining and other processing methods can increase the potential for introduction of human operation error. In addition, for the hydrogel graft, more human operation error may be introduced during the sample detection progress under dry state. For transmission electron microscopy, the sample surface shrinkage will be caused by dehydration process during sample preparation, and this may change the inherent morphology of the sample, so it is difficult to obtain the required information directly. There are two kinds of technologies that can help the transmission electron microscope to achieve the surface morphology differences under dry and wet state and characterize the relationship. First, the optical stereoscopic microscope can be used to detect the hydrogel graft chain in water, and if the observed morphology has large-scale characteristics (> 10 μm), the overall appearance of the optical microscope photograph has a direct reference significance to the result of scanning electron microscope. Second, wet graft copolymer samples can treated with in situ hardening treatment after frozen by liquid nitrogen, and then the water-containing samples can be observed under transmission electron microscope directly. In addition, drying treatment of hydrogel critical point can be expected to maintain the surface morphology of graft copolymers. However, during critical point drying treatment, the introduction used to replace the aqueous solvent will bring morphology changes that similar to the dehydration, and this is because of swelling-deswelling process. The similar results obtained by two different analysis methods have been determined with the morphological images, and finding that the differences between wet and dry graft surfaces is mainly depend on the scale of the surface protrusions, rather than other general natures, and this is related with the initiation grafting rate. The in-depth study on this issue is undergoing. Application of high resolution scanning electron microscope can directly contribute to better access the information on the polymer surface morphology[70] . Application of Lanthanum-boron compound cathode electron gun can make the analysis depth of scanning electron microscope to extend to 30 Å, and meantime, the potential damage to the sample surface is obvious, and more serious to the samples with large surface unevenness. Radiographic inspection can lead to the introduction of artificial illusion, so the detection should be rapid and short in time to decrease the radiographic inspection. Block copolymer surfactant Phase separation, or micro-structural phenomenon is widespread in the block copolymer materials. The driving force of this kind of phase separation is based on the nature of entropy changes and energy. In recent years, the researches in this field have achieved development[43-44, 71] , but there is less development in the researches of the surface characteristics of this kind of materials. Transmission electron microscope is used to observe the surface morphology of block copolymer surfactant, and mainly focus on the surface phase separation. For the stained polymer film, the main information of surface morphology is obtained mainly depends on the scanning electron microscope and transmission electron microscope. The information obtained with transmission electron microscope make from the staining sheet is important for the understanding the noumenon morphology of block copolymer, especially the block copolymer in the region has phase separation[43,72] . Duplication method is very useful in the preparation of transmission electron microscope sample, and it can be used to further identify the X-ray photoelectron spectroscopy conclusions[73] . For the electron microscopy analysis of multiphase polymer systems, scattered electron microscope can be used to improve the contrast, but should pay attention to avoid introducing artificial illusion[74] . In the analysis of block copolymer surfactant with remarkable texture and cracking plane, such as osmium stained polystyrene/polybutadiene blends, using the backscattered electron analysis generated from accelerated electron flow with different energy can observe the microdomains situation in the surface area. Moreover, the analysis depth is controllable. The penetration and sampling depth obtained under 35 kV accelerating voltage are larger than that obtained under 15 kV accelerating voltage, and the sampling depth can be decreased to 100Å. Although the result was obtained from the testing of blend, but it is suitable for the research of copolymer. X-ray photoelectron spectroscopy has considered being the tool with particular value in the research of surface properties of block copolymer. The advantages of X-ray photoelectron spectroscopy in the research is the surface properties (the research subjects are set in 10-100 Å on the surface top), preparation requirements of minimum amount of test specimen, material non-destructive depth sampling capability, and the ability to obtain rich-chemical information. The one of the earliest researches on X-ray photoelectron spectroscopy of block copolymer is the research on polydimethylsiloxane/polystyrene-AB type copolymer surface[75-81 ] . Under all kinds of conditions, the instant surfaces are almost entirely constituted by pure polydimethylsiloxane. The observation of shake-up satellite peaks (π—>π* transfer) in the spectra of polystyrene C-1s X-ray photoelectron spectroscopy showed that the thickness of polydimethylsiloxane surface film is about 13-40 Å, and strongly influenced with nature of the casting solvent. After that, variable-angle X-ray photoelectron spectroscopy technique is also used in the research of same polymer system with lower molecular weight, but the results are totally different with those in the researches of the silane coating dominanted polymer system with higher molecular weight. In addition, in the surface research of X-ray photoelectron spectroscopy of polycarbonate/ polydimethylsiloxane copolymer, the concentration on the surface of polydimethylsiloxane segments is identified. And the study is also performed on polycarbonate/polysulfone copolymer systems. We can obtain the same conclusion that surface properties of block copolymer are greatly determined by the lower surface energy polymeric component in the copolymer system. Except for the X-ray photoelectron spectroscopy, other methods can be used to characterize the surface migration and content of polydimethylsiloxane graft copolymer, such as the contact angle method[79,80-82] . Sessile drop method was used for surface construction of styrene-dimethyl siloxane block copolymer prepared with toluene solution containing polystyrene[82] . The surface tension testing showed that the exits of polystyrene-polydimethylsiloxane-polystyrene “ABA” block copolymers can significantly reduce the surface energy of the original polystyrene, and that may be caused by surface enrichment of silane block copolymer[83] . Polyether-polystyrene block copolymer is used to study the surface/noumenon difference. Transmission electron microscopy characterization of tetrahydrofuran/ polystyrene copolymer fibers containing tetrahydrofuran that prepared with the chloroform solvent showed the tetrahydrofuran was covered with polystyrene[84] . With the increasing of polystyrene content, the lamellar morphology on the surface of polytetrahydrofuran was gradually observed, this is because of the presence of high content of tetrahydrofuran can make the crystalline of polytetrahydrofuran components to reject polystyrene component, and this crystalline behavior become the driving force for the covering of polytetrahydrofuran surface with polystyrene. Contact angle method and the reverse gas chromatography were used to characterize the complex phase separation exits in the system. And reverse gas chromatography is suitable for the surface research of methyl methacrylate-methacrylic acid ester block copolymer. Variable-angle X-ray photoelectron spectroscopy technique was used to study the polyoxyethylene- polystyrene diblock or triblock copolymers[73, 85-87] . The data showed the polystyrene component surface enrichment in two systems, as well as the discrete micro-composition of surface polystyrene and polyoxyethylene, and the electrical interaction and mutual mixing of polyoxyethylene and polystyrene has been confirmed. The interaction with the oxygen-ether bond may lead to the changes of morphology and strength of shake-up satellite peak of polystyrene aromatic ring. And from this, the AB and ABA similar structure observed in the blend system of polyoxyethylene and polystyrene can be explained. X-ray photoelectron spectroscopy surface analysis can be used to analyze the polystyrene/poly(-ethenyl pyrimidinyl) block copolymer. There is no electrical interactions and phase separation between two aromatic functional groups of the polystyrene/poly(-ethenyl pyrimidinyl) block copolymer. But the electrical effects above can be displayed by the random copolymer of styrene and 2-vinylpyrimidine, and can be correspondingly explained by the aromatic ring steric effects (larger in random copolymer and smaller in block copolymer) and electrical effects (compatibility)."
[1]Boretos JW. Contemporary Biomaterials: material and host response, clinical applications, new technology, and legal aspects. Park Ridge, NJ: Noyes Publications. 1984: 232-233.[2]Helmus MH, Hubbell JA. Materials selection. In: Cardiovascular Biomaterials and Biocompatibility. Cardiovascular Pathology. 1993;2(3 Suppl.):53-71.[3]Helmus MN. Designing critical medical devices without failure. In: Spectrum, Diagnostics, Medical Equipment & Supplies, and Oprhalmics. Decision Resources MA: Waltham. 1992:37.[4]Chen BL,Wang DA.Hemocompatibility of biomedical polymeric materials Design of anticoagulant materials. Zhongguo Zuzhi Gongcheng Yanjiu. 2012;16(34): 6393-6396[5]Helmus MN. Outlook for Biomedical Materials. Inc. Decision Resources.1990:12.[6]Von Recum AF. Handbook of Biomaterials Evaluation: Scientific, Technical and Clinical Testing of Implant Materials. New York: Macmillan Publishing Company. 1986:79-97.[7]Helmus MN. Maretials selection for medical devices. In: Specttum, Performance Materials. Decision Resources Inc. 1993:1,21-44.[8]Rashkind WJ, Wagner H. Vascular Catheter Devices: A Study of Safety and Performance. Franklin Research Center, Food and Drug Administration Contract No. 223-5008,1981.[9]Snyder RW, Helmus MN. Vascular prostheses, in Encyclopedia of Medical Devices and Instrumentation. New York: Wiley-Interscience. 1988: 2839-2847.[10]Vandomael M, Ischinger T, Roth R. Angioplasty equipment and supplies: technical considerations. In Practice of Coronary Angioplasty. New York: Springer-Verlang. 1986: 93-127.[11]Schoen FJ. Interventional and Surgical Cardiovascular Pathology: Clinical Correlations and Basic Principles. Philadelphia: W.B. Saunders. 1989:157-158.[12]King MW. Designing fabrics for blood vessel replacement. Canadian Textile J. 1991;108(4):24-30.[13]Guidoin R, Marceau D, Rao TJ, et al. In vitro and in vivo characterization of an impervious polyester arterial prosthesis: the Gelseal Triaxial graft. Biomaterials. 1987; 8(6):433-442.[14]Cook SD, Thomas KA, Brinker MR. Bioactive Ceramic Coatings for Orthopaedic and Dental Implant Applications. In Blood Compatible Materials and Devices: Lancaster: Perspectives Toward the 21st Century, Technomic Publishing. 1991, Chapter 16:279-287.[15]Stokes K. Controlled release of steroid to enhance pacemaker performance. Trans Society for Biomaterials. 1987:52.[16]Canon NH, Graf JE. United States Patent 4606118. 1986.[17]Sullivan SJ, Maki T, Borland KM, et al. Biohybrid artificial pancreas: long-term implantation studies in diabetic, pancreatectomized dogs. Science. 1991;252(5006): 718-721.[18]Andrade JD, Nagaoka S, Cooper S, et al. Surfaces and blood compatibility: current hypotheses. Trans Am Soc Artif Intern Organs. 1987;33(2):75. [19]Eberhart RC, Huo HH, Nelson K. Cardiovascular materials. Materials Research Society. Bulletin. 1981;16(1):50-54.[20]Andrade JD, Hlady V. Protein adsorption and materials biocompatibility: a tutorial review and suggested hypotheses. Adv Polym Sci. 1986;79(1):1-63.[21]Coury AJ, Slaikeu PC, Cahalan PT, et al. Factors and interactions affecting the performance of polyurethane elastomers in medical devices. J Biomater Appl. 1988;3(2): 130-179.[22]Helmus M, Botan EA, Malone J, et al. Sterility and pyrogenicity issues of synthetic vascular grafts. In Kambic H, Kantrowitz A, Sung P, eds. Vascular Graft Update, ASTM Spec. Tech Publ. STP898. Philadelphia: American Society for Testing and Materials. 1986:236-249.[23]Takahara A, Hergenrother RW, Coury AJ, et al. Effect of soft segment chemistry on the biostability of segmented polyurethanes. II. In vitro hydrolytic degradation and lipid sorption. J Biomed Mater Res. 1992;26(6): 801-818.[24]Mueller E, Kammula R, Marlowe D. Regulation of Biomaterials and Medical Devices. MRS bulletin. 1991; 16(9): 39-41.[25]Chen BL, Wang DA. Preparation and mechanism of anticoagulatent biomedical polymer materials with blood compatibility. Zhongguo Zuzhi Gongcheng Yanjiu yu Linchuang Kangfu. 2011;15(29):5507-5510.[26]Szycher M. Thrombosis, hemostasis, and thrombolysis at prosthetic interfaces. In: Szycher Med. Biocompatible Polymers, Metals and Composites. Lancaster, PA: Technomic Pub Co. 1983:1-33.[27]Shimizu T, Kouketsu K, Morishima Y, et al. A new polyvinylchloride blood bag plasticized with lessleachable phthalate ester analogue, di-n-decyl phthalate, for storage of platelets. Transfusion. 1989;29(4):292-297.[28]Park JB. Biomaterials Science and Engineering. New York: Plenum Press. 1984:171-192.[29]Desai NP, Hubbell JA. Biological responses to polyethylene oxide modified polyethylene terephthalate surfaces. J Biomed Mater Res. 1991;25(7):829-843.[30]Nagaoka S, Akashi R. Low-friction hydrophilic surface for medical devices. Biomaterials. 1990;11(6):419-424. [31]Barenberg SA, Brash JL, Narayan R, et al. Degradable materials: perspectives, issues and opportunities. Boca Ration, FL, USA: CRC Press. 1990:11.[32]Greisler HP, Endean ED, Klosak JJ, et al. Polyglactin 910/polydioxanone bicomponent totally resorbabal vascular prostheses. J Vasc Surg. 1988;7(5):697-705.[33]Williams DF. Biocompatibility of Clinical Implant Materials. Boca Raton, FL, USA: CRC Press. 1981:45-61.[34]Levy RJ, Schoen FJ, Flowers WB, et al. Initiation of mineralization in bioprosthetic heart valves: studies of alkaline phosphatase activity and its inhibition by AlCl3 or FeCl3 preincubations. J Biomed Mater Res. 1991;25(8): 905-935.[35]Hoffman AS. Modification of material surfaces to affect how they interact with blood. Ann N Y Acad Sci. 1987;516(1): 96-101.[36]Abele JE. Technical considerations: physical properties of balloon catheters, inflation devices and pressure measurement devices. In: Castaned-Zuniga WR. Transluminal angioplasty. New York: Thieme-Stratton. 1983:20-27.[37]Trilo PM, Andrade JD. Surface modification and evaluation of some commonly used catheter materials. I. Surface properties. J Biomed Mater Res. 1983;17(1):129-147.[38]Trilo PM, Andrade JD. Surface modification and characterization of some commonly used catheter materials. II. Friction characterization. J Biomed Mater Res. 1983; 17(1): 149-165.[39]Salzman EW, Merill EW. Interaction of blood with artificial surfaces, in: Hemostasis and Thrombosis, 2nd ed. Philadelphia, Pa, USA: J.B. Lippincott. 1987:1335-1347.[40]Chenoweth DE. Complement Activation in Extracorporeal Circuits. In: Blood in Contact with Natural and Artificial Surfaces. Ann N Y Acad Sci. 1987;516:306-313.[41]Harrison JA, Colton RJ, White CT, et al. Atomistic Simulation of the Nanoindentation of Diamond and Graphite Surfaces. Mater Res Soc Sym Proc. 1992;239:573.[42]Hubbell JA, Massia SP, Desai NP, et al. Endothelial cell-selective materials for tissue engineering in the vascular graft via a new receptor. Biotechnology. 1991;9(6): 568-572.[43]Gallot BRM. Structure and properties of polymers. In: Advances in Polymer Science, Berlin; New York: Springer-Verlag. 1978:85-156.[44]Noshay A, McGrath JE. Block copolymers: overview and critical survey. New York: Inc., Academic Press. 1977:516.[45]Battared HAJ, Tregear GW. Graft Copolymers. New York: Interscience Publishers. 1967:43.[46]Legge NR. Thermoplastic Elastomers. In: presented at the Applied Polymer Science, Washington, D. C.:Organic Coatings and Plastics Chemistry Division. 1975:394-429.[47]Estes GM, Cooper SL, Tobolsky AV. Block Polymers and Related Heterophase Elsatomers. J Macromol Sci Rev Macromol Chem. 1970;C4(2):313-316.[48]Stannett V. Grafting. Radiat Phys Chem. 1981;18(1-2): 215-222.[49]Cooper SL, Estes GM. Multiphase polymers. ACS. 1979; 176:217-229.[50]Yamakawa S. Surface modification of polyethylene by radiation-induced grafting for adhesive bonding. I. Relationship between adhesive bond strength and surface composition. J Appl Polym Sci. 1976;20(11): 3057-3072.[51]Lodesova D, Pikler A, Foeldesova M, et al. Contribution to the radiation-induced grafting of acrylonitrile and glycolmetacrylate to polypropylene. Radiochem Radioanal Lett. 1978;32(5-6):327-336.[52]Tazuke S, Kimura H. Surface photografting, 2. Modification of polypropylene film surface by graft polymerization of acrylamide. Makrmol Chem Phys. 1978;179(11): 2603-2612.[53]Ikada Y, Iwata H, Horii F, et al. Blood compatibility of hydrophilic polymers, J Biomed Mater Res. 1981;15(5): 697-718.[54]Yamamoto F, Yamakawa S. Surface grafting of polyethylene by mutual irradiation in methyl acrylate vapor. III. Quantitative surface analysis by x-ray photoelectron spectroscopy.J Polymer Sci B Polymer Phys. 1979;17(9): 1581-1590.[55]Ratner BD. Characterization of graft polymers for biomedical applications. J Biomed Mater Res. 1980;14(5): 665-687.[56]Ikada Y. Characterization of Graft Copolymers. Adv Polym Sci. 1978;29(1):47-84.[57]Ratner BD, Weathersby PK, Hoffman AS, et al. Radation-grafted hydrogels for biomaterial applications as studied by the ESCA technique. J Appl Polym Sci. 1978; 22(3):643-664.[58]Yamashita Y. Organic coatings and applied polymer science proceedings. 1982;46:75-78.[59]Holly FJ, Refojo MF. Water Wettability of Hydrogels. Hydrogels for Medical and Related Applications, in ACS Symposium Series. 1976;31:252-266.[60]Everhart DS, Reilley CN. The effects of functional group mobility on quantitative ESCA of plasma modified polymer surfaces.Surf Interface Anal. 1981;3(3):126-133.[61]King RN. Proceedings of the workshop on interfacial phenomena: Research needs and priorities. Washington, D.C.: National Science Foundation. 1979:458-502.[62]Ko YC, Ratner BD, Hoffman AS. Characterization of hydrophilic-hydrophobic polymeric surfaces by contact angle measurements. J Colloid Interface Sci. 981;82(1): 25-37.[63]Azrak RG. Surface Property Variations in Melt-formed Thermo-plastics. J Colloid Interface Sci. 1974;47(3): 779-794.[64]Ducheyne P, van der Perre G, Aubert AE. Biomaterials and biomechanics 1983: proceedings of the Fourth European Conference on Biomaterials. Leuven, Belgium. 1983:2.[65]Yasuda H.Glow discharge polymerization. J Polymer Sci Macromol Rev. 1981;16(1):199-293.[66]Kay E, Dilks A. Plasma polymerization of fluorocarbons in rf capacitively coupled diode system. J Vac Sci Technol. 1981; 18(1):1-11.[67]Boenig HV. Plasma Science and Technology. Ithaca, New York: Cornell University Press, USA Hanser. 1982:299.[68]Hegazy El-Sayed A, Ishigaki I, Rabie A, et al. Study on radiation grafting of acrylic acid onto fluorine-containing polymers. II. Properties of membrane obtained by preirradiation grafting onto poly(tetrafluoroethylene. J Appl Polym Sci. 1981;26(11):3871-3883.[69]Chapiro A. Radiation induced grafting(1977). Radiat Phys Chem. 1977;9(1-3):55-67. [70]Tagawa T, Mori J. Application of the high resolution SEM to the fine structure study of polyethylene. Micron(1969). 1978;9(4):215-221.[71]Gibson PE, Vallance MA, Cooper SL. Development in block copolymers-1. In: Googman I, editor. Development series. London: Elsevier. 1985:217-259.[72]Peter Goetze K, Porter RS. Extrusion degradation of a high molecular weight polystyrene. J Polym Sci C: Polym Symp. 1971;35(1):189-200.[73]Thomas HR, O'Malley JJ. Surface studies on multicomponent polymer systems by X-ray photoelectron spectroscopy. Polystyrene/poly(ethylene oxide) diblock copolymers. Macromolecules. 1979;12(2):323-329.[74]Roche EJ, Thomas EL. Defocus electron microscopy of multiphase polymers: use and misuse. Polymer. 1981; 22(3):333-341.[75]Hobbs SY, Watkins VH. The use of chemical contrast in the SEM analysis of polymer blends. J Polymer Sci B Polymer Phys.1982;20(4):651-658.[76]Short JM, Crystal RG. Amphiphilic heteroarm star copolymers; polystyrene-poly(ethylene oxide);anionic polymerization. Appl Polym Symp. 1971;16:137-151.[77]Sultan JN, Laible RC, McGarry FJ. Microstructure of Two-Phase Polymers. Appl Polym Symp. 1971;16:127-136.[78]Andrade JD, Coleman DL, Gregonis DE. Characterization of polymer surface morphology by scanning electron spectroscopy using backscattered electron imaging. Makromol Chem Rap Commun. 1980;1(2):101-104.[79]Clark DT, Peeling J, O'Malley JM. Application of ESCA to polymer chemistry. VIII. Surface structures of AB block copolymers of polydimethylsiloxane and polystyrene. J Polym Sci Polym Chem. 1976;14(3):543-551.[80]Starnes Jr WH, Schilling FC, Abbås KB, et al. Mechanism for the Formation of Chloromethyl Branches in Poly(vinyl chloride). Macromolecules. 1979;12(4):556-562.[81]McGrath JE, Dwight DW, Riffle JS, et al. Bulk and Surface Segregation in Polycarbonate-Polysulfone and Polycarbonate-Polydimethylsiloxane Block Copolymers. Polymer Preprints, Division of Polymer Chemistry, Inc. of the American Chemical Society. 1979;20(2):528-530.[82]Zana R. The synthesis of poly(silyl-ester)s via hydrosilylation-based polymerization of AB mononmers. Polymer Preprints, Division of Polymer Chemistry, Inc. of the American Chemical Society. 1982;23(1):39.[83]Owen MJ, Kendrick TC. Surface Activity of Polystyrene-Polysiloxane-Polystyrene ABA Block Copolymers. Macromolecules. 1970;3(4):458-461.[84]Gaines Jr GL, Bender GW. Surface Concentration of a Styrene-Dimethylsiloxane Block Copolymer in Mixtures with Polystyrene.Macromolecules. 1972;5(1):82-86.[85]Yamashita Y. Surface Properties of Styrene-Tetrahydrofuran Block Copolymers. J Macromol Sci: A Chem. 1979;13(3):401-413.[86]Ito K, Usami N, Yamashita Y. Syntheses of Methyl Methacrylate-Stearyl Methacrylate Graft Copolymers and Characterization by Inverse Gas Chromatography. Macromolecules. 1980;13(2):216-221.[87]Ronald Thomas H, O'Malley JJ. Surface Studies on Multicomponent Polymer Systems by X-ray Photoelectron Spectroscopy. Polystyrene/Poly(ethylene oxide) Diblock Copolymers. Macromolecules. 1979;12(2):323-329. |
[1] | Li Xinping, Cui Qiuju, Zeng Shuguang, Ran Gaoying, Zhang Zhaoqiang, Liu Xianwen, Fang Wei, Xu Shuaimei. Effect of modification of β-tricalcium phosphate/chitosan hydrogel on growth and mineralization of dental pulp stem cells [J]. Chinese Journal of Tissue Engineering Research, 2021, 25(22): 3493-3499. |
[2] | Liu Liyong, Zhou Lei. Research and development status and development trend of hydrogel in tissue engineering based on patent information [J]. Chinese Journal of Tissue Engineering Research, 2021, 25(22): 3527-3533. |
[3] | Ma Qing, Shi Liyan, Huang Sixue, Zheng Zhangbowen, Zhang Aihua, Zhan Desong, Fu Jiale. Research status and prospect of zirconia ceramics in dental prosthesis [J]. Chinese Journal of Tissue Engineering Research, 2021, 25(22): 3597-3602. |
[4] | Wen Zhijing, Gu Pengzhen, He Xijing, Li Jialiang, Wang Yibin, Wang Yiqun. Development of high molecular polymer polyetherketoneketone and its prospects in medical applications [J]. Chinese Journal of Tissue Engineering Research, 2021, 25(22): 3603-3608. |
[5] | Chen Siyu, Li Yannan, Xie Liying, Liu Siqi, Fan Yurong, Fang Changxing, Zhang Xin, Quan Jiayu, Zuo Lin. Thermosensitive chitosan-collagen composite hydrogel loaded with basic fibroblast growth factor retards ventricular remodeling after myocardial infarction in mice [J]. Chinese Journal of Tissue Engineering Research, 2021, 25(16): 2472-2478. |
[6] | Li Yanle, Yue Xiaohua, Nie Zhen, Zhang Junwei, Li Zhaohui, Nie Weizhi, Jiang Hongjiang. Characteristics and application of bioabsorbable materials in orthopedics [J]. Chinese Journal of Tissue Engineering Research, 2021, 25(16): 2612-2617. |
[7] | Xu Changkui, Pu Xiaobing, Lu Yao, Chen Jiarong, Pan Lei. Safety and antibacterial properties of gentamicin-loaded silk fibroin in meniscus repair [J]. Chinese Journal of Tissue Engineering Research, 2021, 25(10): 1545-1549. |
[8] | Tang Jingfeng, Zhang Jun, You Qi, Liu Yi. The role and mechanism of graphene and its derivatives-related composites in cartilage repair [J]. Chinese Journal of Tissue Engineering Research, 2020, 24(4): 619-624. |
[9] | Liu Haiyan, Hu Yang, Wu Xiuping, Pan Haobo, Jing Xuan. Chitosan-based polysaccharide biomaterial for prevention and treatment of oral diseases [J]. Chinese Journal of Tissue Engineering Research, 2020, 24(4): 631-636. |
[10] | Liu Fei, Zhang Guanxin, Liu Xiaohong, Wang Licheng, Xu Zhiyun. Endothelialization of acellular scaffold from sterilized bovine pericardium [J]. Chinese Journal of Tissue Engineering Research, 2020, 24(28): 4562-4566. |
[11] | Sun Xirao, Sun Baozhai, Zhang Zhenbao. Combination of magnesium ion with mineralized collagen intervenes osteogenic differentiation of mouse preosteoblasts [J]. Chinese Journal of Tissue Engineering Research, 2020, 24(22): 3467-3473. |
[12] | Zhang Xue, Zhang Yang, Cui Fuzhai. Bioactivity of the peptide P17-bone morphogenetic protein-2/nano-hydroxyapatite-mineralized collagen composite [J]. Chinese Journal of Tissue Engineering Research, 2020, 24(22): 3547-3552. |
[13] | Zhou Jian, Tian Zhuang, Tian Qinyu, Luo Xujiang, Peng Liqing, Li Kun, Sui Xiang, Huang Jingxiang, Liu Shuyun, Guo Quanyi, Yao Qi. Properties of gelatin methacrylate/decellularized meniscus extracellular matrix composite hydrogel with different crosslinking densities [J]. Chinese Journal of Tissue Engineering Research, 2020, 24(16): 2493-2499. |
[14] | Liu Yan, Chen Qingyu, Gao Xiang, Gao Junwu. Effect of collagen scaffold on proliferation and osteogenic differentiation of human periodontal ligament stem cells treated by Eucommia ulmoides Oliver leaf extract [J]. Chinese Journal of Tissue Engineering Research, 2020, 24(16): 2537-2543. |
[15] | Hu Kaiwei, Nie Ling, Zhang He, Li Yuzhou, Yang Sheng. Application of α-n-butyl 2-cyanoacrylate medical adhesive for repair of oral mucosal wound of rats [J]. Chinese Journal of Tissue Engineering Research, 2020, 24(16): 2526-2530. |
Viewed | ||||||
Full text |
|
|||||
Abstract |
|
|||||