中国组织工程研究 ›› 2010, Vol. 14 ›› Issue (3): 477-481.doi: 10.3969/j.issn.1673-8225.2010.03.023

• 生物材料基础实验 basic experiments of biomaterials • 上一篇    下一篇

不同质量配比壳聚糖/聚乙烯醇复合材料组织工程支架的制备：结构及性能比较

李沁华，黄  雷，李  慧，方思函   

  1. 暨南大学生物医学工程系，广东省广州市 510632
  • 出版日期:2010-01-15 发布日期:2010-01-15
  • 作者简介:李沁华★，女，1963年生，广东省广州市人，汉族，1987年暨南大学毕业，硕士，副研究员，主要从事组织工程生物材料支架与再生医学方面的研究。 libmejnu@163.com
  • 基金资助:

    广东省211建设项目（50621030）。

Preparation of chitosan/polyvinyl alcohol composite scaffold at different mass ratios: Comparison of structure and characteristics

Li Qin-hua, Huang Lei, Li Hui, Fang Si-han   

  1. Department of Biomedical Engineering, Jinan University, Guangzhou   510632, Guangdong Province, China
  • Online:2010-01-15 Published:2010-01-15
  • About author:Li Qin-hua★, Master, Associate investigator, Department of Biomedical Engineering, Jinan University, Guangzhou 510632, Guangdong Province, China libmejnu@163.com
  • Supported by:

    the 211 Program of Guangdong Province, No. 50621030*

PDF

962

摘要：

背景：聚乙烯醇具有与人体组织相近的含水量、良好的生物相容性和较高的机械强度，适合作为组织工程基质材料。但如何改善其细胞亲和性，是将其作为组织再生支架材料的关键。
目的：制备壳聚糖/聚乙烯醇复合支架，探讨其作为修复人体损伤组织或器官组织工程支架材料的可行性。
方法：将固定相对分子质量和醇解度的聚乙烯醇124与固定脱乙酰度的壳聚糖按不同质量配比复合，分别用成膜法、成颗粒法、冷冻干燥法制备壳聚糖/聚乙烯醇复合支架。测定复合膜的透光率、含水率、膨胀率；测定复合颗粒和复合海绵的含水率；并用扫描电镜观察复合支架横截面的形貌。
结果与结论：通过改变复合支架中壳聚糖与聚乙烯醇和含量，制备7种不同质量配比的复合支架。成膜法制备的复合支架，其透光率为70%~80%，含水率为121.2%~162.5%，膨胀率为60.3%~133.7%；成颗粒法和冷冻干燥法制备的复合支架，其含水率分别为82.0%~461.2%和280.8%~1939.0%。聚乙烯醇与壳聚糖的质量配比为0.75/0.15时，复合支架的综合性能最好。扫描电镜观察显示，聚乙烯醇与壳聚糖的质量配比为0.75/0.15时，用冷冻干燥法制备的复合支架其内部结构规整，呈蓬松纤维状，有较好的力学性能和较高的含水率。

关键词: 聚乙烯醇, 壳聚糖, 复合支架, 组织工程, 生物材料

Abstract:

BACKGROUND: Polyvinyl alcohol (PVA) has similar water content as human tissues, good biocompatibility and high mechanical strength, thereby being utilized as tissue-engineered matrix material. However, the modification in cellular affinity benefits the function as tissue regeneration scaffold materials.
OBJECTIVE: To prepare chitosan (CS) / PVA composite scaffold and explore the feasibility of serving as a scaffold for tissue engineering.
METHODS: Scaffolds of CS/PVA was fabricated by blending PVA-124 with various amounts of CS using film forming, particle forming, and free-drying methods. Water content, light transmittance, and swelling ratio were tested. Scanning electron microscope was used to observe the configuration of the cross section.
RESULTS AND CONCLUSION: A total of 7 different proportional scaffolds were obtained with different PVA and CS dosage. The composite film showed light transmittance between 70%-80%, high water content between 121.2%-162.5% and swelling ratio between 60.3%-133.7%.Composite particle and sponge obtained water content between 82.0%-461.2% and 280.8%- 1 939.0%. Composite scaffold with the amount ratio of PVA 0.75 g/CS 0.15 g exhibited the best performance. Scanning electron microscope showed that at a mass ratio of PVA 0.75 g/CS 0.15 g, the scaffold prepared by freeze-drying method had regular, fluffy inner structure, with good mechanics and high water content.

中图分类号: