Abstract:

BACKGROUND: Due to the complexity and irregularity of bypass obturation of oval root canal and the particular stress of the post and core to the tooth, we have not yet found a reasonable post crown for dental restoration after bypass obturation of the oval root canal.
OBJECTIVE: To compare the flexural capacity of the three kinds of post-and-core repair systems (cobalt-chromium cast post and core, zirconium oxide post andcore, and CAD/CAM-fabricated glass fiber post and core) after bypass obturation of the oval root canal warm gutta. 
METHODS: Ninety mandibular first premolars were selected for bypass obturation of the root canal with Obtura II & System B, and then randomized into three groups that were respectively restored with cobalt-chromium cast post and core, zirconium oxide post and core and CAD/CAM-fabricated glass fiber post and core. After that, cobalt-chromium metal crown was used for full-crown restoration. Fracture strength and fracture type were recorded in different groups. 
RESULTS AND CONCLUSION: The fracture resistance was higher in the cobalt-chromium cast post and core group and zirconium oxide post and core group than the glass fiber post and core group (P < 0.05), and the former two groups had no significant difference. Cobalt-chromium cast post and core was fractured at the root of tooth, and could not be repaired; the zirconium oxide post and core was fractured at the root neck and root of tooth, which was confirmed as reparative fracture; the glass fiber post and core was fractured at the tooth neck, which could be restored. These findings indicate that the cobalt-chromium cast post and core can bear greater occlusal force, but has a higher probability of root fracture; the CAD/CAM-fabricated glass fiber post and core exhibits a lower probability of root fracture

中国组织工程研究杂志出版内容重点：生物材料；骨生物材料; 口腔生物材料; 纳米材料; 缓释材料; 材料相容性；组织工程

Key words: Post and Core Technique, Root Canal Obturation